- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 2.12
- 吸水率 [%]: 0.01
- 缺口冲击强度: 100.0
- 弯曲强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 0.540
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.12 - 2.17 g/cc | 0.0766 - 0.0784 lb/in³ | Average value: 2.14 g/cc Grade Count:20 |
| Water Absorption | 0.0100 - 0.0500 % | 0.0100 - 0.0500 % | Average value: 0.0231 % Grade Count:16 |
| Viscosity | 1.00e+6 - 1.00e+7 cP @Temperature 380 - 380 °C | 1.00e+6 - 1.00e+7 cP @Temperature 716 - 716 °F | Average value: 5.50e+6 cP Grade Count:5 |
| Thickness | 12.7 - 10000 microns | 0.500 - 394 mil | Average value: 1440 microns Grade Count:15 |
| Linear Mold Shrinkage | 0.0200 - 0.0600 cm/cm | 0.0200 - 0.0600 in/in | Average value: 0.0386 cm/cm Grade Count:7 |
| Melt Flow | 1.00 - 36.0 g/10 min | 1.00 - 36.0 g/10 min | Average value: 12.2 g/10 min Grade Count:17 |
| Deformation | 2.40 - 2.70 % | 2.40 - 2.70 % | Average value: 2.55 % Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60.0 - 65.0 | 60.0 - 65.0 | Average value: 60.2 Grade Count:15 |
| Tensile Strength, Ultimate | 22.0 - 39.0 MPa | 3190 - 5660 psi | Average value: 31.9 MPa Grade Count:16 |
| 7.00 - 17.0 MPa @Temperature 250 - 250 °C | 1020 - 2470 psi @Temperature 482 - 482 °F | Average value: 11.0 MPa Grade Count:8 | |
| Elongation at Break | 250 - 410 % | 250 - 410 % | Average value: 356 % Grade Count:16 |
| 400 - 740 % @Temperature 250 - 250 °C | 400 - 740 % @Temperature 482 - 482 °F | Average value: 622 % Grade Count:9 | |
| Modulus of Elasticity | 0.451 - 0.700 GPa | 65.4 - 102 ksi | Average value: 0.484 GPa Grade Count:6 |
| Flexural Modulus | 0.540 - 0.686 GPa | 78.3 - 99.5 ksi | Average value: 0.615 GPa Grade Count:15 |
| Compressive Yield Strength | 5.00 - 6.00 MPa | 725 - 870 psi | Average value: 5.50 MPa Grade Count:5 |
| Izod Impact, Notched | 100 J/cm - NB | 187 ft-lb/in - NB | Grade Count:10 |
| Izod Impact, Unnotched | NB | NB | Grade Count:5 |
| NB - NB @Temperature -40.0 - -40.0 °C | NB - NB @Temperature -40.0 - -40.0 °F | Grade Count:1 | |
| Charpy Impact Unnotched | NB - NB @Temperature -40.0 - -40.0 °C | NB - NB @Temperature -40.0 - -40.0 °F | Grade Count:1 |
| Coefficient of Friction | 0.0400 - 0.250 | 0.0400 - 0.250 | Average value: 0.0924 Grade Count:33 |
| Coefficient of Friction, Static | 0.0500 | 0.0500 | Average value: 0.0500 Grade Count:5 |
| Taber Abrasion, mg/1000 Cycles | 22.5 - 96.8 | 22.5 - 96.8 | Average value: 70.6 Grade Count:15 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+17 - 1.00e+18 ohm-cm | 1.00e+17 - 1.00e+18 ohm-cm | Average value: 8.80e+17 ohm-cm Grade Count:15 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | Average value: 1.00e+17 ohm Grade Count:9 |
| Dielectric Constant | 1.92 - 2.12 | 1.92 - 2.12 | Average value: 2.06 Grade Count:33 |
| Dielectric Strength | 20.0 - 80.0 kV/mm | 508 - 2030 kV/in | Average value: 28.4 kV/mm Grade Count:7 |
| Dissipation Factor | 0.0000100 - 0.00800 | 0.0000100 - 0.00800 | Average value: 0.000249 Grade Count:33 |
| Arc Resistance | 300 sec | 300 sec | Average value: 300 sec Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 - 130 µm/m-°C | 66.7 - 72.2 µin/in-°F | Average value: 126 µm/m-°C Grade Count:15 |
| 140 - 250 µm/m-°C @Temperature 100 - 200 °C | 77.8 - 139 µin/in-°F @Temperature 212 - 392 °F | Average value: 195 µm/m-°C Grade Count:1 | |
| Specific Heat Capacity | 1.05 J/g-°C | 0.250 BTU/lb-°F | Average value: 1.05 J/g-°C Grade Count:8 |
| Thermal Conductivity | 0.220 - 0.251 W/m-K | 1.53 - 1.74 BTU-in/hr-ft²-°F | Average value: 0.248 W/m-K Grade Count:9 |
| Melting Point | 300 - 315 °C | 572 - 599 °F | Average value: 307 °C Grade Count:14 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Average value: 260 °C Grade Count:15 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:33 |
| Oxygen Index | 95.0 % | 95.0 % | Average value: 95.0 % Grade Count:33 |