- 密度 [g/cm3]: 2.12
- 弯曲强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 0.600
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.12 - 2.17 g/cc | 0.0766 - 0.0784 lb/in³ | |
| Water Absorption | <= 0.050 % | <= 0.050 % | |
| Linear Mold Shrinkage | 0.040 - 0.060 cm/cm | 0.040 - 0.060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | |
| Tensile Strength, Ultimate | 22.0 - 28.0 MPa | 3190 - 4060 psi | |
| Elongation at Break | >= 300 % | >= 300 % | |
| >= 400 % @Temperature 250 °C | >= 400 % @Temperature 482 °F | ||
| Flexural Modulus | 0.600 - 0.650 GPa | 87.0 - 94.3 ksi | |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Izod Impact, Unnotched | NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | (Notch not specified) |
| Charpy Impact Unnotched | NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | Notch not specified |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+17 ohm-cm @Temperature 23.0 - 150 °C | >= 1.00e+17 ohm-cm @Temperature 73.4 - 302 °F | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 2.1 @Frequency 50 Hz | 2.1 @Frequency 50 Hz | |
| Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm | 864 kV/in @Thickness 0.0394 in | |
| Dissipation Factor | 0.00030 - 0.0080 @Frequency 50 Hz, Temperature 23.0 - 150 °C | 0.00030 - 0.0080 @Frequency 50 Hz, Temperature 73.4 - 302 °F | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 µm/m-°C @Temperature 20.0 °C | 66.7 µin/in-°F @Temperature 68.0 °F | |
| 140 µm/m-°C @Temperature 100 °C | 77.8 µin/in-°F @Temperature 212 °F | ||
| 250 µm/m-°C @Temperature 200 °C | 139 µin/in-°F @Temperature 392 °F | ||
| Melting Point | >= 300 °C | >= 572 °F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous |
| Oxygen Index | >= 95 % | >= 95 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 350 - 410 °C | 662 - 770 °F | |