- 密度 [g/cm3]: 1.74
- 缺口冲击强度: 2.72
- 拉伸强度 [MPa]: 87.0
- 弯曲模量 [MPa]: 10.34
- 热变形温度 [℃]: 251.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 |
| 1.75 g/cc | 0.0632 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.012 cm/cm @Time 86400 sec | 0.010 - 0.012 in/in @Time 24.0 hour | ASTM D955 |
| 0.011 cm/cm @Time 86400 sec | 0.011 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.018 - 0.020 cm/cm @Time 86400 sec | 0.018 - 0.020 in/in @Time 24.0 hour | ASTM D955 |
| 0.019 cm/cm @Time 86400 sec | 0.019 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ASTM D638 |
| 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D638 | |
| 88.0 MPa | 12800 psi | ISO 527 | |
| Tensile Strength, Yield | 87.0 MPa | 12600 psi | ASTM D638 |
| 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 | |
| 89.0 MPa | 12900 psi | ISO 527 | |
| Elongation at Break | 4.8 % | 4.8 % | ASTM D638 |
| 4.8 % | 4.8 % | Type I, 5 mm/min; ASTM D638 | |
| 4.9 % | 4.9 % | ISO 527 | |
| Elongation at Yield | 4.5 % | 4.5 % | ASTM D638 |
| 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D638 | |
| 4.6 % | 4.6 % | ISO 527 | |
| Tensile Modulus | 11.58 GPa | 1680 ksi | 1 mm/min; ISO 527 |
| 15.16 GPa | 2199 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 319 MPa | 46300 psi | ISO 178 |
| Flexural Modulus | 10.34 GPa | 1500 ksi | ASTM D790 |
| 10.34 GPa | 1500 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 18.8 GPa | 2730 ksi | ISO 178 | |
| Izod Impact, Notched | 2.72 J/cm | 5.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.3 J/cm | 19.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J | 13.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 8.00 J | 5.90 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 77.4 µm/m-°C @Temperature -40.0 - 40.0 °C | 43.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 78.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 43.3 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 12.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 6.67 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 12.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 7.00 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C | 484 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 255 °C @Thickness 3.20 mm | 491 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 222 °C @Thickness 3.20 mm | 432 °F @Thickness 0.126 in | unannealed; ASTM D648 | |