- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 1.69
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 11.7
- 断裂伸长率 [%]: 8.00
- 弯曲强度 [MPa]: 12.0
- 弯曲模量 [MPa]: 0.192
- 硬度: 62.0
- 热变形温度 [℃]: 48.0
- 脆化温度 [℃]: -62.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.69 - 1.88 g/cc | 0.0611 - 0.0679 lb/in³ | Average value: 1.78 g/cc Grade Count:98 |
| Water Absorption | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.0396 % Grade Count:77 |
| Moisture Absorption at Equilibrium | 0.000 - 0.500 % | 0.000 - 0.500 % | Average value: 0.110 % Grade Count:11 |
| Water Absorption at Saturation | 0.000 - 0.0500 % | 0.000 - 0.0500 % | Average value: 0.0362 % Grade Count:8 |
| Particle Size | 5.00 µm | 5.00 µm | Average value: 5.00 µm Grade Count:14 |
| Particle Mesh Size | 14.0 Mesh | 14.0 Mesh | Average value: 14.0 Mesh Grade Count:14 |
| Viscosity | 1200 - 2.00e+7 cP @Temperature 232 - 260 °C | 1200 - 2.00e+7 cP @Temperature 450 - 500 °F | Average value: 2.12e+6 cP Grade Count:52 |
| 1200 - 2.00e+7 cP @Shear Rate 50.0 - 100 1/s | 1200 - 2.00e+7 cP @Shear Rate 50.0 - 100 1/s | Average value: 2.12e+6 cP Grade Count:52 | |
| Viscosity Test | 0.850 - 170 cm³/g @Temperature 30.0 - 30.0 °C | 0.850 - 170 cm³/g @Temperature 86.0 - 86.0 °F | Average value: 46.5 cm³/g Grade Count:7 |
| Linear Mold Shrinkage | 0.0100 - 0.0350 cm/cm | 0.0100 - 0.0350 in/in | Average value: 0.0255 cm/cm Grade Count:29 |
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.0300 cm/cm | 0.00800 - 0.0300 in/in | Average value: 0.0226 cm/cm Grade Count:6 |
| Melt Flow | 0.200 - 40.0 g/10 min | 0.200 - 40.0 g/10 min | Average value: 8.69 g/10 min Grade Count:91 |
| Ash | 0.000 - 5.00 % | 0.000 - 5.00 % | Average value: 2.50 % Grade Count:4 |
| Fiber Count | 328 - 2060 dtex | 295 - 1850 denier | Average value: 1040 dtex Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 62.0 - 115 | 62.0 - 115 | Average value: 92.3 Grade Count:3 |
| Hardness, Shore D | 47.0 - 82.0 | 47.0 - 82.0 | Average value: 71.8 Grade Count:59 |
| Ball Indentation Hardness | 62.0 - 105 MPa | 8990 - 15200 psi | Average value: 92.5 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 12.0 - 714 MPa | 1740 - 104000 psi | Average value: 130 MPa Grade Count:80 |
| 1.00 - 39.0 MPa @Temperature 50.0 - 100 °C | 145 - 5660 psi @Temperature 122 - 212 °F | Average value: 14.6 MPa Grade Count:6 | |
| 1.00 - 39.0 MPa @Strain 20.0 - 20.0 % | 145 - 5660 psi @Strain 20.0 - 20.0 % | Average value: 14.6 MPa Grade Count:6 | |
| Tensile Strength, Yield | 11.7 - 141 MPa | 1700 - 20500 psi | Average value: 42.0 MPa Grade Count:86 |
| Elongation at Break | 0.000 - 800 % | 0.000 - 800 % | Average value: 171 % Grade Count:103 |
| Elongation at Yield | 0.000 - 25.0 % | 0.000 - 25.0 % | Average value: 10.5 % Grade Count:72 |
| Creep Strength | 3.70 - 3.70 MPa @Temperature 60.0 - 90.0 °C | 537 - 537 psi @Temperature 140 - 194 °F | Average value: 3.70 MPa Grade Count:4 |
| 3.70 - 3.70 MPa @Time 360000 - 3.60e+6 sec | 537 - 537 psi @Time 100 - 1000 hour | Average value: 3.70 MPa Grade Count:4 | |
| Modulus of Elasticity | 0.180 - 7.00 GPa | 26.1 - 1020 ksi | Average value: 1.55 GPa Grade Count:87 |
| 0.0500 - 1.40 GPa @Temperature 50.0 - 100 °C | 7.25 - 203 ksi @Temperature 122 - 212 °F | Average value: 0.422 GPa Grade Count:5 | |
| Tenacity | 0.371 - 0.416 N/tex | 4.20 - 4.71 g/denier | Average value: 0.380 N/tex Grade Count:5 |
| Flexural Yield Strength | 8.00 - 207 MPa | 1160 - 30000 psi | Average value: 51.1 MPa Grade Count:49 |
| Flexural Modulus | 0.192 - 8.55 GPa | 27.8 - 1240 ksi | Average value: 1.61 GPa Grade Count:55 |
| Compressive Yield Strength | 3.00 - 172 MPa | 435 - 24900 psi | Average value: 50.4 MPa Grade Count:32 |
| Izod Impact, Notched | 0.400 J/cm - NB | 0.750 ft-lb/in - NB | Average value: 3.37 J/cm Grade Count:54 |
| Izod Impact, Unnotched | 2.67 J/cm - NB | 5.00 ft-lb/in - NB | Average value: 19.6 J/cm Grade Count:33 |
| Charpy Impact Unnotched | 25.5 J/cm² - NB | 121 ft-lb/in² - NB | Average value: 26.5 J/cm² Grade Count:8 |
| 21.0 - 26.0 J/cm² @Temperature -30.0 - -30.0 °C | 99.9 - 124 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 22.8 J/cm² Grade Count:4 | |
| Charpy Impact, Notched | 0.600 - 1000 J/cm² | 2.86 - 4760 ft-lb/in² | Average value: 2.92 J/cm² Grade Count:12 |
| 0.500 - 1.10 J/cm² @Temperature -30.0 - -30.0 °C | 2.38 - 5.24 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.700 J/cm² Grade Count:6 | |
| Tensile Impact Strength | 140 - 210 kJ/m² | 66.6 - 99.9 ft-lb/in² | Average value: 170 kJ/m² Grade Count:3 |
| Coefficient of Friction | 0.100 - 0.540 | 0.100 - 0.540 | Average value: 0.263 Grade Count:59 |
| Coefficient of Friction, Static | 0.100 - 0.550 | 0.100 - 0.550 | Average value: 0.293 Grade Count:55 |
| Taber Abrasion, mg/1000 Cycles | 5.00 - 33.0 | 5.00 - 33.0 | Average value: 11.2 Grade Count:50 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 5.00e+16 ohm-cm | 100 - 5.00e+16 ohm-cm | Average value: 1.34e+15 ohm-cm Grade Count:79 |
| Surface Resistance | 100 - 1.00e+16 ohm | 100 - 1.00e+16 ohm | Average value: 4.18e+14 ohm Grade Count:37 |
| Dielectric Constant | 3.20 - 33.5 | 3.20 - 33.5 | Average value: 7.94 Grade Count:63 |
| Dielectric Strength | 0.394 - 150 kV/mm | 10.0 - 3810 kV/in | Average value: 39.9 kV/mm Grade Count:53 |
| Dissipation Factor | 0.00500 - 0.370 | 0.00500 - 0.370 | Average value: 0.126 Grade Count:47 |
| Dielectric Loss Index | 0.0250 - 0.165 | 0.0250 - 0.165 | Average value: 0.100 Grade Count:3 |
| Arc Resistance | 50.0 sec | 50.0 sec | Average value: 50.0 sec Grade Count:3 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 344 V Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 17.0 - 67.0 J/g | 7.31 - 28.8 BTU/lb | Average value: 47.0 J/g Grade Count:28 |
| CTE, linear | 36.0 - 216 µm/m-°C | 20.0 - 120 µin/in-°F | Average value: 139 µm/m-°C Grade Count:73 |
| 86.0 - 370 µm/m-°C @Temperature -40.0 - 85.0 °C | 47.8 - 206 µin/in-°F @Temperature -40.0 - 185 °F | Average value: 185 µm/m-°C Grade Count:5 | |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | Average value: 100 µm/m-°C Grade Count:3 |
| Specific Heat Capacity | 1.17 - 1.90 J/g-°C | 0.280 - 0.454 BTU/lb-°F | Average value: 1.30 J/g-°C Grade Count:51 |
| 1.60 - 1.60 J/g-°C @Temperature 100 - 100 °C | 0.382 - 0.382 BTU/lb-°F @Temperature 212 - 212 °F | Average value: 1.60 J/g-°C Grade Count:18 | |
| Thermal Conductivity | 0.110 - 0.300 W/m-K | 0.763 - 2.08 BTU-in/hr-ft²-°F | Average value: 0.181 W/m-K Grade Count:58 |
| Melting Point | 117 - 180 °C | 243 - 356 °F | Average value: 162 °C Grade Count:104 |
| Crystallization Temperature | 12.0 - 146 °C | 53.6 - 295 °F | Average value: 127 °C Grade Count:28 |
| Maximum Service Temperature, Air | 116 - 400 °C | 240 - 752 °F | Average value: 229 °C Grade Count:27 |
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 - 152 °C | 118 - 306 °F | Average value: 102 °C Grade Count:46 |
| Deflection Temperature at 1.8 MPa (264 psi) | 26.7 - 168 °C | 80.0 - 335 °F | Average value: 78.8 °C Grade Count:71 |
| Vicat Softening Point | 61.0 - 171 °C | 142 - 340 °F | Average value: 132 °C Grade Count:29 |
| Minimum Service Temperature, Air | -60.0 - -40.0 °C | -76.0 - -40.0 °F | Average value: -50.0 °C Grade Count:6 |
| Brittleness Temperature | -62.0 - 10.0 °C | -79.6 - 50.0 °F | Average value: -21.8 °C Grade Count:16 |
| Glass Transition Temp, Tg | -48.0 - -18.0 °C | -54.4 - -0.400 °F | Average value: -37.1 °C Grade Count:62 |
| Decomposition Temperature | 375 - 410 °C | 707 - 770 °F | Average value: 392 °C Grade Count:32 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:73 |
| Oxygen Index | 42.0 - 95.0 % | 42.0 - 95.0 % | Average value: 52.6 % Grade Count:61 |
| Shrinkage | 3.00 - 16.3 % | 3.00 - 16.3 % | Average value: 6.24 % Grade Count:5 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.40 - 1.42 | 1.40 - 1.42 | Average value: 1.41 Grade Count:9 |
| Gloss | 25.0 - 40.0 % | 25.0 - 40.0 % | Average value: 30.0 % Grade Count:3 |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 215 - 232 °C | 419 - 450 °F | Average value: 224 °C Grade Count:3 |
| Nozzle Temperature | 200 - 255 °C | 392 - 491 °F | Average value: 226 °C Grade Count:12 |
| Die Temperature | 210 - 260 °C | 410 - 500 °F | Average value: 231 °C Grade Count:18 |
| Melt Temperature | 116 - 250 °C | 240 - 482 °F | Average value: 215 °C Grade Count:24 |
| Head Temperature | 210 - 250 °C | 410 - 482 °F | Average value: 226 °C Grade Count:18 |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Average value: 70.0 °C Grade Count:12 |