- 吸水率 [%]: 0.04
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 5.515
- 热变形温度 [℃]: 132.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 - 1.88 g/cc | 1.84 - 1.88 g/cc | ASTM D792 |
| Bulk Density | 0.961 g/cc | 0.0347 lb/in³ | |
| Water Absorption | 0.040 - 0.060 % @Time 86400 sec | 0.040 - 0.060 % @Time 24.0 hour | Immersion; ASTM D570 |
| Viscosity | 800000 - 1.30e+6 cP @Shear Rate 100 1/s, Temperature 232 °C | 800000 - 1.30e+6 cP @Shear Rate 100 1/s, Temperature 450 °F | Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.035 cm/cm @Time 86400 sec | 0.012 - 0.035 in/in @Time 24.0 hour | |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.030 cm/cm @Time 86400 sec | 0.0080 - 0.030 in/in @Time 24.0 hour | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 74 - 79 | 74 - 79 | ASTM D2240 |
| Tensile Strength at Break | 38.0 - 55.0 MPa | 5510 - 7980 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 - 55.0 MPa | 4930 - 7980 psi | ASTM D638 |
| Elongation at Break | 0.00 - 20 % | 0.00 - 20 % | ASTM D638 |
| Elongation at Yield | 0.00 - 4.0 % | 0.00 - 4.0 % | ASTM D638 |
| Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 360000 sec | 537 psi @Temperature 194 °F, Time 100 hour | Deflection = 3.3%; Flexural Creep |
| 3.70 MPa @Temperature 90.0 °C, Time 3.60e+6 sec | 537 psi @Temperature 194 °F, Time 1000 hour | Deflection = 3.4%; Flexural Creep | |
| 3.70 MPa @Temperature 60.0 °C, Time 360000 sec | 537 psi @Temperature 140 °F, Time 100 hour | Deflection = 1.5%; Flexural Creep | |
| 3.70 MPa @Temperature 60.0 °C, Time 3.60e+6 sec | 537 psi @Temperature 140 °F, Time 1000 hour | Deflection = 1.7%; Flexural Creep | |
| Tensile Modulus | 3.102 - 5.171 GPa | 449.9 - 750.0 ksi | ASTM D638 |
| Flexural Strength | 138 - 207 MPa @Strain 5.00 % | 20000 - 30000 psi @Strain 5.00 % | ASTM D790 |
| Flexural Modulus | 5.515 - 6.895 GPa | 799.9 - 1000 ksi | ASTM D790 |
| Compressive Strength | 138 - 172 MPa | 20000 - 24900 psi | ASTM D695 |
| Izod Impact, Notched | 0.400 - 0.801 J/cm | 0.750 - 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 - 5.34 J/cm | 5.00 - 10.0 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.12 | 0.12 | vs. steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.18 | 0.18 | vs. steel; ASTM D1894 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm @Temperature 20.0 °C | 1.00e+11 ohm-cm @Temperature 68.0 °F | 65% RH; ASTM D257 |
| Dielectric Constant | 28.3 @Frequency 1.00e+8 Hz | 28.3 @Frequency 1.00e+8 Hz | ASTM D150 |
| 33.5 @Frequency 100 Hz | 33.5 @Frequency 100 Hz | ASTM D150 | |
| Dissipation Factor | 0.060 - 0.080 @Frequency 100 Hz | 0.060 - 0.080 @Frequency 100 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 - 45.0 µm/m-°C | 20.0 - 25.0 µin/in-°F | ASTM D696 |
| Melting Point | 165 - 172 °C | 329 - 342 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 - 149 °C | 270 - 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 - 127 °C | 219 - 261 °F | ASTM D648 |
| Glass Transition Temp, Tg | -40.0 - -38.0 °C @Frequency 1.00 Hz | -40.0 - -36.4 °F @Frequency 1.00 Hz | DMA |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt loss / in air; TGA |
| 410 °C | 770 °F | 1% wt loss / in nitrogen; TGA | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 44 % | 44 % | ASTM D2868 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| 195 - 220 °C | 383 - 428 °F | Tube Extrusion | |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| 210 - 240 °C | 410 - 464 °F | Tube Extrusion | |
| Front Barrel Temperature | 200 - 240 °C | 392 - 464 °F | Injection Molding |
| 210 - 240 °C | 410 - 464 °F | Tube Extrusion | |
| Nozzle Temperature | 200 - 240 °C | 392 - 464 °F | Injection Molding |
| Die Temperature | 210 - 250 °C | 410 - 482 °F | Tube Extrusion |
| Head Temperature | 210 - 240 °C | 410 - 464 °F | Tube Extrusion |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Injection Molding |