- 密度 [g/cm3]: 1.78
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 0.900
- 热变形温度 [℃]: 100.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.78 g/cc | 0.0643 lb/in³ | ISO 1183 | ||
Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
6.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 6.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 30.0 MPa | 4350 psi | 50mm/min; ASTM D638 | ||
Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50mm/min; ASTM D638 | ||
Elongation at Break | 400 % | 400 % | 50mm/min; ASTM D638 | ||
Flexural Strength | 37.0 MPa | 5370 psi | 2mm/min; ASTM D790 | ||
Flexural Modulus | 0.900 GPa | 131 ksi | 2mm/min; ASTM D790 | ||
Thermal Properties | Metric | English | Comments | ||
Melting Point | 160 °C | 320 °F | ASTM D3418 | ||
Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | |||
Vicat Softening Point | 150 °C | 302 °F | 1 kg load; ISO 306 | ||
Flammability, UL94 | V-0 | V-0 | |||
Oxygen Index | >= 44 % @Thickness 3.00 mm | >= 44 % @Thickness 0.118 in | limiting (sheet); ASTM D2863 | ||
Descriptive Properties | |||||
Form | Granules |