- 密度 [g/cm3]: 1.78
- 拉伸强度 [MPa]: 42.0
- 弯曲模量 [MPa]: 2.20
- 热变形温度 [℃]: 147.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | ISO 1183 | ||
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 35 % | 35 % | 50mm/min; ASTM D638 | ||
| Elongation at Yield | 7.0 % | 7.0 % | 50mm/min; ASTM D638 | ||
| Flexural Modulus | 2.20 GPa | 319 ksi | 2mm/min; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 174 °C | 345 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | 44 % @Thickness 3.00 mm | 44 % @Thickness 0.118 in | limiting (sheet); ASTM D2863 | ||
| Shrinkage | 3.0 % | 3.0 % | |||
| Descriptive Properties | |||||
| Form | Pellets | ||||