- 密度 [g/cm3]: 1.76
- 缺口冲击强度: 0.58
- 弯曲模量 [MPa]: 11.79
- 热变形温度 [℃]: 165.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 |
| 1.769 g/cc | 0.06391 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.040 % | 0.040 % | 23°C / 50% RH; ISO 62 |
| 0.030 % @Time 86400 sec | 0.030 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm @Time 86400 sec | 0.0036 in/in @Time 24.0 hour | ISO 294 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec | 0.0030 - 0.0050 in/in @Time 24.0 hour | ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.013 cm/cm @Time 86400 sec | 0.010 - 0.013 in/in @Time 24.0 hour | ASTM D 955 |
| 0.0116 cm/cm @Time 86400 sec | 0.0116 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 67.0 MPa | 9720 psi | ISO 527 |
| 78.0 MPa | 11300 psi | ASTM D 638 | |
| Elongation at Break | 0.60 % | 0.60 % | ISO 527 |
| 0.80 % | 0.80 % | ASTM D 638 | |
| Tensile Modulus | 14.27 GPa | 2070 ksi | 50 mm/min; ASTM D 638 |
| 14.5 GPa | 2100 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 127 MPa | 18400 psi | ASTM D 790 |
| 147 MPa | 21300 psi | ISO 178 | |
| Flexural Modulus | 11.79 GPa | 1710 ksi | ASTM D 790 |
| 20.92 GPa | 3034 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C | 1.09 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 2.02 J/cm @Temperature 23.0 °C | 3.78 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 11.0 J @Temperature 23.0 °C | 8.11 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 31.3 µm/m-°C @Temperature -40.0 - 40.0 °C | 17.4 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 31.3 µm/m-°C @Temperature -40.0 - 40.0 °C | 17.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 86.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 47.9 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 86.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 47.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 165 °C @Thickness 3.20 mm | 329 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 159 °C @Thickness 3.20 mm | 318 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |