- 密度 [g/cm3]: 1.78
- 弯曲模量 [MPa]: 14.82
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D792 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
Tensile Modulus | 17.07 GPa | 2476 ksi | 50 mm/min; ASTM D638 |
Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
Flexural Modulus | 14.82 GPa | 2149 ksi | ASTM D790 |