- 熔体流动速率 [g/10min]: 4.0
- 拉伸强度 [MPa]: 50.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 | ||
Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec | <= 0.040 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
Linear Mold Shrinkage, Flow | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |||
Melt Flow | 4.0 - 6.0 g/10 min @Load 10.0 kg, Temperature 230 °C | 4.0 - 6.0 g/10 min @Load 22.0 lb, Temperature 446 °F | ASTM D1238 | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore D | 72 - 78 @Thickness 2.00 mm, Time 1.00 sec | 72 - 78 @Thickness 0.0787 in, Time 0.000278 hour | ASTM D2240 | ||
Tensile Strength at Break | 30.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 4350 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
Tensile Strength, Yield | 50.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 7250 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
Elongation at Break | 20 - 300 % @Thickness 2.00 mm, Temperature 23.0 °C | 20 - 300 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
Elongation at Yield | 5.0 - 10 % @Thickness 2.00 mm, Temperature 23.0 °C | 5.0 - 10 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
Tensile Modulus | 1.70 - 2.50 GPa @Thickness 2.00 mm, Temperature 23.0 °C | 247 - 363 ksi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 1.0 mm/min; ASTM D638 | ||
Impact | 150 - 250 @Thickness 4.00 mm | 150 - 250 @Thickness 0.157 in | J/m Charpy Notched Impact Strength; 2 m/s; ASTM D6110 | ||
Coefficient of Friction, Dynamic | 0.15 - 0.35 | 0.15 - 0.35 | vs. Itself; ASTM D1894 | ||
Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | vs. Itself; ASTM D1894 | ||
Taber Abrasion, mg/1000 Cycles | 5.0 - 10 @Load 1.00 kg | 5.0 - 10 @Load 2.20 lb | CS-10 Wheel; ASTM D4060 | ||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 | ||
Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 | ||
Dielectric Constant | 7.0 - 10 @Frequency 1000 Hz, Temperature 23.0 °C | 7.0 - 10 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D150 | ||
Dielectric Strength | 0.787 - 0.984 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C | 20.0 - 25.0 kV/in @Thickness 0.0394 in, Temperature 73.4 °F | ASTM D149 | ||
Thermal Properties | Metric | English | Comments | ||
Heat of Fusion | 50.0 - 60.0 J/g | 21.5 - 25.8 BTU/lb | Crystallization Heat; ASTM D3417 | ||
55.0 - 65.0 J/g | 23.7 - 28.0 BTU/lb | ASTM D3417 | |||
CTE, linear, Parallel to Flow | 140 µm/m-°C @Temperature 0.000 - 40.0 °C | 77.8 µin/in-°F @Temperature 32.0 - 104 °F | ASTM D696 | ||
Specific Heat Capacity | 1.20 J/g-°C @Temperature 23.0 °C | 0.287 BTU/lb-°F @Temperature 73.4 °F | ASTM E968 | ||
1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ASTM E968 | |||
Thermal Conductivity | 0.200 W/m-K @Temperature 23.0 °C | 1.39 BTU-in/hr-ft²-°F @Temperature 73.4 °F | ASTM C177 | ||
Melting Point | 170 - 174 °C | 338 - 345 °F | ASTM D3418 | ||
Crystallization Temperature | 137 - 145 °C | 279 - 293 °F | Peak, DSC; ASTM D3418 | ||
Vicat Softening Point | 135 - 145 °C | 275 - 293 °F | Rate A (50°C/h), Loading 2 (50 N); ASTM D1525 | ||
Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 | ||
Flammability, UL94 | V-0 @Thickness 0.100 mm | V-0 @Thickness 0.00394 in | UL 94 | ||
Oxygen Index | 44 % @Thickness 3.00 mm | 44 % @Thickness 0.118 in | ASTM D2863 | ||
Descriptive Properties | |||||
Availability | Africa & Middle East | ||||
Asia Pacific | |||||
Europe | |||||
North America | |||||
South America | |||||
Features | High Viscosity | ||||
Homopolymer | |||||
Generic | PVDF | ||||
Processing Method | Compression Molding | ||||
Extrusion |