- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 1.76
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 20.0
- 弯曲强度 [MPa]: 21.0
- 热变形温度 [℃]: 81.0
- 脆化温度 [℃]: -35.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 |
Water Absorption | <= 0.040 % | <= 0.040 % | ISO 62 (method 1) |
Melt Flow | 1.2 g/10 min @Load 5.00 kg, Temperature 230 °C | 1.2 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
4.0 g/10 min @Load 10.0 kg, Temperature 230 °C | 4.0 g/10 min @Load 22.0 lb, Temperature 446 °F | ASTM D1238 | |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 61 @Thickness 2.00 mm | 61 @Thickness 0.0787 in | ASTM D2240 |
Tensile Strength, Ultimate | 21.0 - 30.0 MPa | 3050 - 4350 psi | 50 mm/min; ASTM D638 |
Tensile Strength, Yield | 20.0 - 30.0 MPa | 2900 - 4350 psi | 50 mm/min; ASTM D638 |
Elongation at Break | 250 - 500 % | 250 - 500 % | 50 mm/min; ASTM D638 |
Elongation at Yield | 10 - 15 % | 10 - 15 % | 50 mm/min; ASTM D638 |
Modulus of Elasticity | 0.700 GPa | 102 ksi | 1 mm/min; ASTM D638 |
Izod Impact, Notched | 12.0 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 22.5 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | Notched V 10 mm; ASTM D256 |
Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | ASTM D1894 |
Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | ASTM D1894 |
Taber Abrasion, mg/1000 Cycles | 5.0 - 15 | 5.0 - 15 | CS10 / 1 kg |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483 |
Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483 |
Thermal Properties | Metric | English | Comments |
Heat of Fusion | 34.0 J/g | 14.6 BTU/lb | Crystallization Heat |
37.0 J/g | 15.9 BTU/lb | 80°C to end of melting | |
CTE, linear | 130 - 160 µm/m-°C @Temperature 20.0 °C | 72.2 - 88.9 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
Specific Heat Capacity | 1.20 J/g-°C | 0.287 BTU/lb-°F | |
1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ||
Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
Melting Point | 171 °C | 340 °F | Crystallinity by DSC; ASTM D 3418 |
Crystallization Temperature | 138 °C | 280 °F | |
Maximum Service Temperature, Air | 320 - 340 °C | 608 - 644 °F | Thermal Stability via TGA : beginning - and at 1% weight loss in air |
Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C @Thickness 4.00 mm | 178 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C @Thickness 4.00 mm | 120 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
Vicat Softening Point | 154 °C @Load 1.00 kg, Thickness 4.00 mm | 309 °F @Load 2.20 lb, Thickness 0.157 in | ISO 306 |
Brittleness Temperature | -35.0 °C | -31.0 °F | ASTM D746A |
Glass Transition Temp, Tg | -28.0 °C | -18.4 °F | DMTA |
Oxygen Index | 46 % @Thickness 3.00 mm | 46 % @Thickness 0.118 in | sheet; ASTM D2863 |