- 密度 [g/cm3]: 2.19
- 断裂伸长率 [%]: 5.50
- 弯曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.19 - 2.27 g/cc | 0.0791 - 0.0820 lb/in³ | BS2782:Pt6 | ||
| Deformation | 6.4 % | 6.4 % | Permanent Deformation; ASTM D621 | ||
| 9.0 % @Time 3600 sec, Pressure 14.2 MPa | 9.0 % @Time 1.00 hour, Pressure 2060 psi | ASTM D621 | |||
| 9.2 % @Time 3600 sec, Pressure 5.00 MPa | 9.2 % @Time 1.00 hour, Pressure 725 psi | 150°C; ASTM D621 | |||
| 12.4 % @Pressure 14.2 MPa, Time 86400 sec | 12.4 % @Pressure 2060 psi, Time 24.0 hour | ASTM D621 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 64 - 68 | 64 - 68 | ASTM D2240 | ||
| Tensile Strength | 11.0 - 15.0 MPa | 1600 - 2180 psi | Moulding Direction; BS2782:Pt3 | ||
| Elongation at Break | 120 - 270 % | 120 - 270 % | Moulding Direction; BS2782:Pt3 | ||
| Flexural Yield Strength | 5.50 MPa @Strain 0.200 % | 798 psi @Strain 0.200 % | ASTM D790 | ||
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 | ||
| Compressive Strength | 1.80 MPa @Strain 0.200 %, Temperature 150 °C | 261 psi @Strain 0.200 %, Temperature 302 °F | ASTM D695 | ||
| 7.20 MPa @Strain 0.200 %, Temperature 23.0 °C | 1040 psi @Strain 0.200 %, Temperature 73.4 °F | ASTM D695 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ASTM D257 | ||
| Dielectric Constant | 2.36 @Frequency 60.0 Hz | 2.36 @Frequency 60.0 Hz | ASTM D150 | ||
| 2.85 @Frequency 1.00e+6 Hz | 2.85 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Dielectric Strength | 12.9 kV/mm | 328 kV/in | Air; ASTM D149 | ||
| 34.2 kV/mm | 869 kV/in | Oil; ASTM D149 | |||
| Dissipation Factor | 0.0028 @Frequency 1.00e+6 Hz | 0.0028 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 0.0718 @Frequency 60.0 Hz | 0.0718 @Frequency 60.0 Hz | ASTM D150 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 136 µm/m-°C @Temperature 23.0 - 200 °C | 75.6 µin/in-°F @Temperature 73.4 - 392 °F | ASTM D696 | ||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 200 °C | 46.7 µin/in-°F @Temperature 73.4 - 392 °F | ASTM D696 | ||
| Thermal Conductivity | 0.410 W/m-K | 2.85 BTU-in/hr-ft²-°F | Moulding Direction; ASTM C177 | ||
| Melting Point | 327 °C | 621 °F | ASTM D3417 | ||
| Maximum Service Temperature, Air | 260 °C | 500 °F | |||
| 300 °C | 572 °F | Short Periods | |||
| Minimum Service Temperature, Air | -200 °C | -328 °F | |||
| Flash Point | 630 °C | 1170 °F | ASTM D1929 | ||
| Oxygen Index | 98 - 100 % | 98 - 100 % | ASTM D2863 | ||
| Descriptive Properties | |||||
| Color | Off-White | ||||