- 密度 [g/cm3]: 2.24
- 弯曲强度 [MPa]: 19.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.24 g/cc | 0.0809 lb/in³ | Sintered moldings; ASTM D4894/D4895 |
| Apparent Bulk Density | 0.820 g/cc | 0.0296 lb/in³ | DIN 53 466 |
| Linear Mold Shrinkage | 0.017 cm/cm @Thickness 80.0 mm | 0.017 in/in @Thickness 3.15 in | sheet; ASTM D4894 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength, Ultimate | 19.0 MPa @Thickness 2.00 mm | 2760 psi @Thickness 0.0787 in | ASTM D4894 |
| Elongation at Break | 320 % @Thickness 2.00 mm | 320 % @Thickness 0.0787 in | ASTM D4894 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 30.0 - 100 °C | 55.6 µin/in-°F @Temperature 86.0 - 212 °F | |
| 130 µm/m-°C @Temperature 30.0 - 200 °C | 72.2 µin/in-°F @Temperature 86.0 - 392 °F | ||
| 150 µm/m-°C @Temperature 30.0 - 300 °C | 83.3 µin/in-°F @Temperature 86.0 - 572 °F | ||
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52 612 |