- 密度 [g/cm3]: 2.11
- 弯曲强度 [MPa]: 13.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 2.11 g/cc | 0.0762 lb/in³ | Sintered moldings; ASTM D4894/D4895 |
Apparent Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | DIN 53 466 |
Linear Mold Shrinkage | 0.033 cm/cm @Thickness 80.0 mm | 0.033 in/in @Thickness 3.15 in | sheet; ASTM D4894 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 66 | 66 | ASTM D2240 |
Tensile Strength, Ultimate | 13.0 MPa @Thickness 2.00 mm | 1890 psi @Thickness 0.0787 in | ASTM D4894 |
Elongation at Break | 70 % @Thickness 2.00 mm | 70 % @Thickness 0.0787 in | ASTM D4894 |