- 密度 [g/cm3]: 3.05
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.05 - 3.12 g/cc | 0.110 - 0.113 lb/in³ | molded; ASTM D792 |
| Deformation | 3.0 - 5.0 % @Pressure 13.7 MPa, Time 86400 sec | 3.0 - 5.0 % @Pressure 1990 psi, Time 24.0 hour | after 24hr relaxation; ASTM D621 |
| 8.0 - 11 % @Pressure 13.7 MPa, Time 86400 sec | 8.0 - 11 % @Pressure 1990 psi, Time 24.0 hour | ASTM D621 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 - 67 | 62 - 67 | molded; ASTM D2240 |
| Tensile Strength | 23.0 - 28.0 MPa | 3340 - 4060 psi | molded; ASTM D4745 |
| Elongation at Break | 200 - 250 % | 200 - 250 % | molded; ASTM D4745 |
| Compressive Yield Strength | 7.00 - 9.00 MPa @Strain 1.00 % | 1020 - 1310 psi @Strain 1.00 % | ASTM D695 |
| Coefficient of Friction, Dynamic | 0.13 | 0.13 | ASTM D1894 |
| K (wear) Factor | 9.00 - 13.0 x 10-8 mm³/N-M | 4.47 - 6.45 x 10-10 in³-min/ft-lb-hr | at PV 100; ASTM D3702 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 - 115 µm/m-°C | 55.6 - 63.9 µin/in-°F | ASTM D696 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Minimum Service Temperature, Air | -200 °C | -328 °F | |