- 密度 [g/cm3]: 2.18
- 拉伸强度 [MPa]: 20.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.18 g/cc | 0.0788 lb/in³ | ISO 1183-1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 58 | 58 | DIN 53505 | ||
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527-1/-2 | ||
| Elongation at Break | 300 % | 300 % | ISO 527-1/-2 | ||
| Modulus of Elasticity | 0.750 GPa | 109 ksi | |||
| Compressive Yield Strength | 4.50 MPa @Strain 1.00 % | 653 psi @Strain 1.00 % | dry; ISO 604 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179-1/1eA | ||
| Coefficient of Friction, Dynamic | 0.080 | 0.080 | |||
| Sand Slurry | 21 | 21 | µm/km | ||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 2.0 @Frequency 100 Hz | 2.0 @Frequency 100 Hz | IEC 60250 | ||
| 2.1 @Frequency 1.00e+6 Hz | 2.1 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 | ||
| Dielectric Loss Index | 0.00010 @Frequency 1.00e+6 Hz | 0.00010 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.00030 @Frequency 100 Hz | 0.00030 @Frequency 100 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 160 µm/m-°C @Temperature 23.0 - 100 °C | 88.9 µin/in-°F @Temperature 73.4 - 212 °F | |||
| Melting Point | 321 °C | 610 °F | ISO 11357-1 | ||
| Maximum Service Temperature, Air | 260 °C @Time 7.20e+7 sec | 500 °F @Time 20000 hour | |||
| 300 °C @Time <=86400 sec | 572 °F @Time <=24.0 hour | ||||
| Minimum Service Temperature, Air | -200 °C | -328 °F | |||
| Glass Transition Temp, Tg | 127 °C | 261 °F | ISO 11357-1 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Compliance Properties | Metric | English | Comments | ||
| FDA | Yes | Yes | |||
| Descriptive Properties | |||||
| Color | Natural | ||||