- 密度 [g/cm3]: 2.24
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.24 g/cc | 0.0809 lb/in³ | ASTM 1457-62 T |
| Deformation | 7.0 - 14 % | 7.0 - 14 % | 14 MPa, 100 h, 23°C; ASTM D621-59 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 30.0 MPa | 4350 psi | ASTM 1457-62 T |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM 1457-62 T |
| Elongation at Break | 370 % | 370 % | ASTM 1457-62 T |
| Coefficient of Friction, Dynamic | 0.145 - 0.17 | 0.145 - 0.17 | v = 1 m/s |
| 0.14 - 0.21 | 0.14 - 0.21 | v = 1.9 m/s | |
| Abrasion | 2.1 | 2.1 | mm of depth after 200 hrs load duration; Partner Material ST 50 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | DIN 53482 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 µm/m-°C @Temperature 100 °C | 55.6 µin/in-°F @Temperature 212 °F | DIN 52328 |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 |