- 密度 [g/cm3]: 3.2
- 缺口冲击强度: 1.4
- 拉伸强度 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.20 g/cc | 0.116 lb/in³ | ISO 1183 |
| Filler Content | 40 % | 40 % | Bronze Filler |
| Particle Size | 40 µm | 40 µm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ISO 868 |
| Ball Indentation Hardness | 40.0 MPa | 5800 psi | ISO 2039-1 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527 |
| Elongation at Break | 260 % | 260 % | ISO 527 |
| Izod Impact, Notched | 1.40 J/cm | 2.62 ft-lb/in | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.10e+16 ohm-cm | 8.10e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 5.50e+16 ohm | 5.50e+16 ohm | IEC 60093 |
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0020 | 0.0020 | IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C | 36.1 µin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 360 °C | 680 °F | Molding |
| Back Pressure | 50.0 - 70.0 MPa | 7250 - 10200 psi | Molding Pressure |