- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.55
- 拉伸强度 [MPa]: 90.0
- 断裂伸长率 [%]: 56.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 3.70
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 - 1.44 g/cc | 0.0444 - 0.0520 lb/in³ | Average value: 1.37 g/cc Grade Count:38 |
| Filler Content | 30.0 - 33.0 % | 30.0 - 33.0 % | Average value: 31.5 % Grade Count:6 |
| Water Absorption | 0.500 - 7.00 % | 0.500 - 7.00 % | Average value: 4.03 % Grade Count:28 |
| Moisture Absorption at Equilibrium | 1.00 - 2.50 % | 1.00 - 2.50 % | Average value: 1.92 % Grade Count:20 |
| Water Absorption at Saturation | 3.50 - 6.50 % | 3.50 - 6.50 % | Average value: 5.07 % Grade Count:7 |
| Viscosity Measurement | 0.400 - 155 | 0.400 - 155 | Average value: 124 Grade Count:5 |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00369 cm/cm Grade Count:35 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0130 cm/cm | 0.00500 - 0.0130 in/in | Average value: 0.00772 cm/cm Grade Count:27 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 80.0 - 270 MPa | 11600 - 39200 psi | Average value: 180 MPa Grade Count:22 |
| Tensile Strength, Ultimate | 45.0 - 210 MPa | 6530 - 30500 psi | Average value: 144 MPa Grade Count:36 |
| 90.0 - 105 MPa @Temperature 110 - 150 °C | 13100 - 15200 psi @Temperature 230 - 302 °F | Average value: 97.5 MPa Grade Count:2 | |
| 90.0 - 105 MPa @Time 1.80e+7 - 7.20e+7 sec | 13100 - 15200 psi @Time 5000 - 20000 hour | Average value: 97.5 MPa Grade Count:2 | |
| Tensile Strength, Yield | 90.0 - 162 MPa | 13100 - 23500 psi | Average value: 121 MPa Grade Count:7 |
| Elongation at Break | 2.00 - 35.0 % | 2.00 - 35.0 % | Average value: 5.02 % Grade Count:35 |
| Elongation at Yield | 4.00 - 6.00 % | 4.00 - 6.00 % | Average value: 4.56 % Grade Count:7 |
| Modulus of Elasticity | 1.80 - 11.0 GPa | 261 - 1600 ksi | Average value: 8.01 GPa Grade Count:30 |
| Flexural Yield Strength | 56.0 - 270 MPa | 8120 - 39200 psi | Average value: 215 MPa Grade Count:15 |
| Flexural Modulus | 3.70 - 9.50 GPa | 537 - 1380 ksi | Average value: 8.26 GPa Grade Count:14 |
| Izod Impact, Notched | 0.550 - 1.50 J/cm | 1.03 - 2.81 ft-lb/in | Average value: 1.04 J/cm Grade Count:4 |
| Izod Impact, Notched (ISO) | 6.20 - 21.0 kJ/m² | 2.95 - 9.99 ft-lb/in² | Average value: 12.5 kJ/m² Grade Count:6 |
| Charpy Impact Unnotched | 2.50 J/cm² - NB | 11.9 ft-lb/in² - NB | Average value: 6.54 J/cm² Grade Count:31 |
| 2.40 J/cm² - NB @Temperature -40.0 - 30.0 °C | 11.4 ft-lb/in² - NB @Temperature -40.0 - 86.0 °F | Average value: 5.27 J/cm² Grade Count:28 | |
| Charpy Impact, Notched | 0.400 - 2.50 J/cm² | 1.90 - 11.9 ft-lb/in² | Average value: 1.10 J/cm² Grade Count:30 |
| 0.200 - 1.00 J/cm² @Temperature -30.0 - 30.0 °C | 0.952 - 4.76 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 0.732 J/cm² Grade Count:23 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 - 1.00e+15 ohm-cm | 1.00e+11 - 1.00e+15 ohm-cm | Average value: 1.52e+14 ohm-cm Grade Count:26 |
| Surface Resistance | 1.00e+10 - 1.00e+15 ohm | 1.00e+10 - 1.00e+15 ohm | Average value: 5.55e+13 ohm Grade Count:20 |
| Dielectric Strength | 21.0 - 60.0 kV/mm | 533 - 1520 kV/in | Average value: 31.3 kV/mm Grade Count:20 |
| Dissipation Factor | 0.0200 | 0.0200 | Average value: 0.0200 Grade Count:4 |
| Comparative Tracking Index | 425 - 650 V | 425 - 650 V | Average value: 552 V Grade Count:27 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 80.0 µm/m-°C | 11.1 - 44.4 µin/in-°F | Average value: 26.9 µm/m-°C Grade Count:21 |
| CTE, linear, Transverse to Flow | 45.0 - 110 µm/m-°C | 25.0 - 61.1 µin/in-°F | Average value: 75.5 µm/m-°C Grade Count:19 |
| Melting Point | 200 - 310 °C | 392 - 590 °F | Average value: 262 °C Grade Count:35 |
| Maximum Service Temperature, Air | 90.0 - 250 °C | 194 - 482 °F | Average value: 164 °C Grade Count:24 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 - 250 °C | 419 - 482 °F | Average value: 231 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 285 °C | 158 - 545 °F | Average value: 223 °C Grade Count:38 |
| Deflection Temperature at 8.0 MPa | 50.0 - 200 °C | 122 - 392 °F | Average value: 138 °C Grade Count:19 |
| Vicat Softening Point | 230 - 252 °C | 446 - 486 °F | Average value: 244 °C Grade Count:3 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:26 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 753 °C Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 241 - 310 °C | 466 - 590 °F | Average value: 288 °C Grade Count:5 |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Average value: 87.3 °C Grade Count:5 |
| Drying Temperature | 79.4 - 80.0 °C | 175 - 176 °F | Average value: 79.9 °C Grade Count:4 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 4.25 hour Grade Count:4 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.156 % Grade Count:3 |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | Average value: 91.5 MPa Grade Count:4 |