- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 0.35
- 缺口冲击强度: 1.66
- 拉伸强度 [MPa]: 140.0
- 断裂伸长率 [%]: 270
- 弯曲强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.76
- 热变形温度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 - 1.72 g/cc | 0.0567 - 0.0621 lb/in³ | Average value: 1.67 g/cc Grade Count:16 |
| Filler Content | 45.0 - 60.0 % | 45.0 - 60.0 % | Average value: 53.8 % Grade Count:8 |
| Water Absorption | 0.350 - 5.00 % | 0.350 - 5.00 % | Average value: 2.30 % Grade Count:12 |
| Moisture Absorption at Equilibrium | 1.10 - 1.20 % | 1.10 - 1.20 % | Average value: 1.18 % Grade Count:5 |
| Water Absorption at Saturation | 3.00 - 4.00 % | 3.00 - 4.00 % | Average value: 3.50 % Grade Count:4 |
| Viscosity | 8000 - 160000 cP @Temperature 277 - 322 °C | 8000 - 160000 cP @Temperature 531 - 612 °F | Average value: 73600 cP Grade Count:1 |
| 8000 - 160000 cP @Frequency 10.0 - 10000 Hz | 8000 - 160000 cP @Frequency 10.0 - 10000 Hz | Average value: 73600 cP Grade Count:1 | |
| Linear Mold Shrinkage | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | Average value: 0.00229 cm/cm Grade Count:14 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.00900 cm/cm | 0.00200 - 0.00900 in/in | Average value: 0.00489 cm/cm Grade Count:11 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 198 - 350 MPa | 28700 - 50800 psi | Average value: 281 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 30.0 - 280 MPa | 4350 - 40600 psi | Average value: 221 MPa Grade Count:17 |
| 150 - 160 MPa @Temperature 80.0 - 80.0 °C | 21800 - 23200 psi @Temperature 176 - 176 °F | Average value: 124 MPa Grade Count:2 | |
| 110 - 125 MPa @Temperature 110 - 150 °C | 16000 - 18100 psi @Temperature 230 - 302 °F | Average value: 124 MPa Grade Count:2 | |
| 110 - 125 MPa @Time 1.80e+7 - 7.20e+7 sec | 16000 - 18100 psi @Time 5000 - 20000 hour | Average value: 124 MPa Grade Count:2 | |
| 25.0 - 195 MPa @Strain 0.500 - 8.00 % | 3630 - 28300 psi @Strain 0.500 - 8.00 % | Average value: 124 MPa Grade Count:1 | |
| 25.0 - 195 MPa @Temperature 60.0 - 120 °C | 3630 - 28300 psi @Temperature 140 - 248 °F | Average value: 124 MPa Grade Count:1 | |
| Tensile Strength, Yield | 140 - 265 MPa @Temperature -20.0 - 80.0 °C | 20300 - 38400 psi @Temperature -4.00 - 176 °F | Average value: 203 MPa Grade Count:1 |
| Elongation at Break | 2.00 - 4.00 % | 2.00 - 4.00 % | Average value: 2.50 % Grade Count:18 |
| 2.30 - 2.80 % @Temperature 80.0 - 80.0 °C | 2.30 - 2.80 % @Temperature 176 - 176 °F | Average value: 2.55 % Grade Count:2 | |
| Modulus of Elasticity | 13.0 - 22.5 GPa | 1890 - 3260 ksi | Average value: 18.3 GPa Grade Count:12 |
| 10.0 - 13.0 GPa @Temperature 80.0 - 80.0 °C | 1450 - 1890 ksi @Temperature 176 - 176 °F | Average value: 11.5 GPa Grade Count:2 | |
| Flexural Yield Strength | 270 - 450 MPa | 39200 - 65300 psi | Average value: 367 MPa Grade Count:11 |
| 290 - 290 MPa @Temperature 80.0 - 80.0 °C | 42100 - 42100 psi @Temperature 176 - 176 °F | Average value: 290 MPa Grade Count:2 | |
| Flexural Modulus | 1.76 - 20.0 GPa | 255 - 2900 ksi | Average value: 15.0 GPa Grade Count:11 |
| 13.0 - 13.0 GPa @Temperature 80.0 - 80.0 °C | 1890 - 1890 ksi @Temperature 176 - 176 °F | Average value: 13.0 GPa Grade Count:2 | |
| Izod Impact, Notched | 1.66 - 1.87 J/cm | 3.10 - 3.50 ft-lb/in | Average value: 1.77 J/cm Grade Count:3 |
| Izod Impact, Notched (ISO) | 13.0 - 17.0 kJ/m² | 6.19 - 8.09 ft-lb/in² | Average value: 14.3 kJ/m² Grade Count:3 |
| Izod Impact, Unnotched (ISO) | 76.0 - 80.0 kJ/m² @Temperature -30.0 - -30.0 °C | 36.2 - 38.1 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 78.0 kJ/m² Grade Count:2 |
| Charpy Impact Unnotched | 8.60 - 11.5 J/cm² | 40.9 - 54.7 ft-lb/in² | Average value: 10.1 J/cm² Grade Count:12 |
| 7.60 - 10.5 J/cm² @Temperature -30.0 - 30.0 °C | 36.2 - 50.0 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 8.97 J/cm² Grade Count:10 | |
| Charpy Impact, Notched | 1.30 - 5.00 J/cm² | 6.19 - 23.8 ft-lb/in² | Average value: 2.89 J/cm² Grade Count:12 |
| 1.10 - 4.50 J/cm² @Temperature -30.0 - 30.0 °C | 5.24 - 21.4 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 2.82 J/cm² Grade Count:10 | |
| Puncture Energy | 31.0 - 31.0 J @Temperature -30.0 - -30.0 °C | 22.9 - 22.9 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 31.0 J Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00e+11 - 1.00e+15 ohm-cm | 5.00e+11 - 1.00e+15 ohm-cm | Average value: 1.25e+14 ohm-cm Grade Count:6 |
| Surface Resistance | 1.00e+12 - 1.50e+17 ohm | 1.00e+12 - 1.50e+17 ohm | Average value: 3.00e+16 ohm Grade Count:5 |
| Dielectric Strength | 18.9 - 40.0 kV/mm | 480 - 1020 kV/in | Average value: 25.7 kV/mm Grade Count:5 |
| Comparative Tracking Index | 55.0 - 600 V | 55.0 - 600 V | Average value: 493 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.6 - 20.0 µm/m-°C | 7.00 - 11.1 µin/in-°F | Average value: 16.5 µm/m-°C Grade Count:7 |
| CTE, linear, Transverse to Flow | 40.0 - 87.0 µm/m-°C | 22.2 - 48.3 µin/in-°F | Average value: 54.5 µm/m-°C Grade Count:6 |
| Melting Point | 238 - 265 °C | 460 - 509 °F | Average value: 254 °C Grade Count:16 |
| Maximum Service Temperature, Air | 100 - 230 °C | 212 - 446 °F | Average value: 172 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 - 257 °C | 473 - 495 °F | Average value: 249 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 - 255 °C | 437 - 491 °F | Average value: 235 °C Grade Count:16 |
| Deflection Temperature at 8.0 MPa | 195 - 235 °C | 383 - 455 °F | Average value: 221 °C Grade Count:7 |
| Flammability, UL94 | HB | HB | Grade Count:10 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 20.0 - 80.0 °C | 68.0 - 176 °F | Average value: 57.5 °C Grade Count:4 |
| Nozzle Temperature | 271 - 310 °C | 520 - 590 °F | Average value: 296 °C Grade Count:3 |
| Melt Temperature | 260 - 320 °C | 500 - 608 °F | Average value: 293 °C Grade Count:6 |
| Mold Temperature | 71.1 - 120 °C | 160 - 248 °F | Average value: 94.3 °C Grade Count:4 |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Average value: 79.9 °C Grade Count:6 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 4.17 hour Grade Count:6 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.155 % Grade Count:4 |
| Injection Pressure | 34.5 - 150 MPa | 5000 - 21800 psi | Average value: 113 MPa Grade Count:6 |
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | Average value: 60.0 MPa Grade Count:4 |
| Back Pressure | 0.345 - 3.00 MPa | 50.0 - 435 psi | Average value: 1.67 MPa Grade Count:5 |
| Screw Speed | 25.0 - 120 rpm | 25.0 - 120 rpm | Average value: 42.1 rpm Grade Count:3 |