- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 6.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 77 | 77 | Conditioned; ISO 868 |
| 84 | 84 | ISO 868 | |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Conditioned; ISO R 527 |
| 130 MPa | 18900 psi | ISO R 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO R 527 |
| 10 % | 10 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | Conditioned; ISO 178 |
| 5.50 GPa | 798 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/1A |
| 11.0 kJ/m² | 5.23 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/IeU |
| 5.50 J/cm² | 26.2 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/IeA |
| 0.800 J/cm² | 3.81 ft-lb/in² | Conditioned; ISO 179/IeA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | Conditioned; CEI 60243-1 |
| 32.0 kV/mm | 813 kV/in | CEI 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | CEI 60112/Solution A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 35.0 µm/m-°C | 19.4 µin/in-°F | ASTM E831 |
| Melting Point | 243 °C | 469 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-2/AF |