- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 8.0
- 拉伸强度 [MPa]: 50.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.0 % | 8.0 % | ISO 62 | ||
| Moisture Absorption | 2.50 % | 2.50 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 | ||
| 75.0 MPa | 10900 psi | dry; ISO 527-1/-2 | |||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 | ||
| 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 10 % | 10 % | dry; ISO 527-1/-2 | ||
| 10 % | 10 % | dry; ISO 527-1/-2 | |||
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |||
| Elongation at Yield | 4.0 % | 4.0 % | dry; ISO 527-1/-2 | ||
| 15 % | 15 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 1.60 GPa | 232 ksi | conditioned; ISO 527-1/-2 | ||
| 3.60 GPa | 522 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | dry; ISO 179/1eU | ||
| 10.0 J/cm² | 47.6 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 7.00 J/cm² @Temperature 30.0 °C | 33.3 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.50 J/cm² | 7.14 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | dry; IEC 60250 | ||
| 3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | dry; IEC 60250 | |||
| 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | conditioned; IEC 60250 | |||
| 8.0 @Frequency 100 Hz | 8.0 @Frequency 100 Hz | conditioned; IEC 60250 | |||
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | conditioned; IEC 60243-1 | ||
| 28.0 kV/mm | 711 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS | ||
| 200 °C | 392 °F | short term; EMS | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-0 | V-0 | IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| Oxygen Index | 35 % | 35 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Automotive | Automotive electr. and electronics, lighting | ||||
| Electricals & Electronics | Cables & Tubes | ||||
| Connectors | |||||
| Electrical appliances | |||||
| Electrical equipment | |||||
| Energy distribution | |||||
| Lighting | |||||
| Form | Granules | ||||
| Processing | Injection Molding | ||||
| Special Characteristics | Flame retardant | ||||