- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 4.5
- 拉伸强度 [MPa]: 110.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.5 % | 4.5 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 150 MPa | 21800 psi | conditioned; ISO 2039-1 | ||
| 205 MPa | 29700 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 100 MPa | 14500 psi | conditioned; ISO 527-1/-2 | ||
| 180 MPa | 26100 psi | dry; ISO 527-1/-2 | |||
| Tensile Strength, Yield | 110 MPa | 16000 psi | conditioned; ISO 527-1/-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 | ||
| 8.0 % | 8.0 % | conditioned; ISO 527-1/-2 | |||
| Elongation at Yield | 4.0 % | 4.0 % | conditioned; ISO 527-1/-2 | ||
| Tensile Modulus | 6.20 GPa | 899 ksi | conditioned; ISO 527-1/-2 | ||
| 10.0 GPa | 1450 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | dry; ISO 179/1eU | ||
| 8.00 J/cm² | 38.1 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 6.00 J/cm² @Temperature 30.0 °C | 28.6 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| 6.50 J/cm² @Temperature 30.0 °C | 30.9 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.20 J/cm² | 5.71 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.600 J/cm² @Temperature 30.0 °C | 2.86 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| 0.800 J/cm² @Temperature 30.0 °C | 3.81 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | conditioned; IEC 60243-1 | ||
| 25.0 kV/mm | 635 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 475 V | 475 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 100 - 130 °C | 212 - 266 °F | long term; EMS | ||
| 200 °C | 392 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 130 °C | 266 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Cooling and climate control | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Heating systems | ||||
| Processing | Injection Molding | ||||
| Product Attributes | High viscosity | ||||
| Special Characteristics | Improved heat resistance | ||||