- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 5.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.0 % | 5.0 % | ISO 62 | ||
| Moisture Absorption | 1.80 % | 1.80 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 180 MPa | 26100 psi | conditioned; ISO 2039-1 | ||
| 275 MPa | 39900 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 165 MPa | 23900 psi | conditioned; ISO 527-1/-2 | ||
| 230 MPa | 33400 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 | ||
| 2.8 % | 2.8 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 9.50 GPa | 1380 ksi | conditioned; ISO 527-1/-2 | ||
| 13.0 GPa | 1890 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | dry; ISO 179/1eU | ||
| 8.50 J/cm² | 40.4 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 6.00 J/cm² @Temperature 30.0 °C | 28.6 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| 6.50 J/cm² @Temperature 30.0 °C | 30.9 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | dry; ISO 179/1eA | ||
| 3.50 J/cm² | 16.7 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 3.00 J/cm² @Temperature 30.0 °C | 14.3 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 3.50 J/cm² @Temperature 30.0 °C | 16.7 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | conditioned; IEC 60243-1 | ||
| 29.0 kV/mm | 737 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 120 - 130 °C | 248 - 266 °F | long term; EMS | ||
| 220 °C | 428 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Form | Granules | ||||
| Product Attributes | Long Fiber Reinforced | ||||