- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.39
- 弯曲模量 [MPa]: 8.75
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | |
| Viscosity Measurement | 0.40 - 0.52 | 0.40 - 0.52 | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0052 cm/cm | 0.0052 in/in | |
| Melt Flow | 2.0 g/10 min @Load 0.325 kg, Temperature 270 °C | 2.0 g/10 min @Load 0.716 lb, Temperature 518 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 195 MPa | 28300 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 245 MPa | 35500 psi | |
| Flexural Modulus | 8.75 GPa | 1270 ksi | |
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature -20.0 °C | 35.7 ft-lb/in² @Temperature -4.00 °F | |
| 8.50 J/cm² @Temperature 23.0 °C | 40.4 ft-lb/in² @Temperature 73.4 °F | ||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -20.0 °C | 3.81 ft-lb/in² @Temperature -4.00 °F | |
| 1.10 J/cm² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ||
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | |
| Dielectric Strength | 60.0 kV/mm | 1520 kV/in | |
| Comparative Tracking Index | 650 V | 650 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Vicat Softening Point | 252 °C | 486 °F | B |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| Glow Wire Test | 960 °C | 1760 °F | at 3 mm |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi | |