- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.8
- 缺口冲击强度: 1.33
- 断裂伸长率 [%]: 82.7
- 弯曲模量 [MPa]: 2.65
- 硬度: 111.0
- 热变形温度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Water Absorption | 1.8 % @Time 86400 sec | 1.8 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm | 0.016 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Yield | 50 % | 50 % | ASTM D638 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.65 GPa | 385 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm, Temperature -40.0 °C | 2.50 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 |
| 6.41 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | NB @Thickness 3.17 mm | NB @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C | 44.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Unannealed; ASTM D648 |