- 密度 [g/cm3]: 1.41
- 热变形温度 [℃]: 290.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Viscosity Test | 85 cm³/g | 85 cm³/g | Viscosity Number | ||
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 210 MPa | 30500 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | PLC 2; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 290 °C | 554 °F | 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Glass Transition Temperature (10°C/min); ISO 11357-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 0.900 mm | 284 °F @Thickness 0.0354 in | UL746B | ||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL746B | |||
| UL RTI, Mechanical with Impact | 120 °C @Thickness 0.900 mm | 248 °F @Thickness 0.0354 in | UL746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | UL746B | |||
| UL RTI, Mechanical without Impact | 120 °C @Thickness 0.900 mm | 248 °F @Thickness 0.0354 in | UL746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Oxygen Index | 22 % | 22 % | ISO 4589-1/-2 | ||
| Glow Wire Test | 675 °C @Thickness 0.750 mm | 1250 °F @Thickness 0.0295 in | Glow Wire Flammability Index; IEC 60695-2-12 | ||
| 700 °C @Thickness 0.750 mm | 1290 °F @Thickness 0.0295 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
| 725 °C @Thickness 3.00 mm | 1340 °F @Thickness 0.118 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||