- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 11.0
- 拉伸强度 [MPa]: 60.0
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 | ||
| Water Absorption | 11 % | 11 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | Humidity Absorption; Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 | ||
| Elongation at Yield | 20 % | 20 % | ISO 527-1/-2 | ||
| Tensile Modulus | 1.85 GPa | 268 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 2.60 J/cm² @Temperature -30.0 °C | 12.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 7.50 J/cm² @Temperature 23.0 °C | 35.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | IEC 60250 | ||
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0012 @Frequency 100 Hz | 0.0012 @Frequency 100 Hz | IEC 60250 | ||
| 0.0019 @Frequency 1e+6 Hz | 0.0019 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 475 V | 475 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 160 µm/m-°C @Temperature 20.0 °C | 88.9 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 180 µm/m-°C @Temperature 20.0 °C | 100 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 250 °C | 482 °F | 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Glass Transition Temperature (10°C/min); ISO 11357-1/-2 | ||
| Oxygen Index | 27 % | 27 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| High Impact or Impact Modified | Yes | ||||
| Injection Molding | Yes | ||||
| Other Extrusion | Yes | ||||
| Platable | Yes | ||||
| Profile Extrusion | Yes | ||||
| Without Fillers | Yes | ||||