- 密度 [g/cm3]: 1.28
- 缺口冲击强度: 0.52
- 拉伸强度 [MPa]: 78.0
- 弯曲模量 [MPa]: 2.80
- 热变形温度 [℃]: 276.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 | |
| Moisture Absorption | 1.80 % | 1.80 % | 50% RH, 24 hrs; ASTM D570 |
| 2.70 % | 2.70 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec | >= 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec | 0.020 - 0.040 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
| 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 5.9 % | 5.9 % | Type I, 5 mm/min; ASTM D638 |
| 6.6 % | 6.6 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 5.8 % | 5.8 % | Type I, 5 mm/min; ASTM D638 |
| 6.5 % | 6.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| 3.13 GPa | 454 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 101 MPa | 14600 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | 2 mm/min; ISO 178 |
| 2.96 GPa | 429 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.520 J/cm | 0.974 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.24 J/cm | 17.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 56.0 kJ/m² | 26.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C | 2.21 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.32 | 0.32 | ASTM D3702 Modified |
| K (wear) Factor | 22.2 x 10-8 mm³/N-M | 11.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature -30.0 - 30.0 °C | 55.6 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 92.6 µm/m-°C @Temperature -30.0 - 30.0 °C | 51.4 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 276 °C | 529 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 283 °C @Thickness 3.20 mm | 541 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 151 °C @Thickness 3.20 mm | 304 °F @Thickness 0.126 in | unannealed; ASTM D648 | |