- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 2.0
- 弯曲模量 [MPa]: 7.60
- 热变形温度 [℃]: 260.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.32 g/cc @Temperature 23.0 °C | 0.0477 lb/in³ @Temperature 73.4 °F | ISO 1183 | ||
Filler Content | 20 % | 20 % | ISO 1172 | ||
Water Absorption | 2.0 - 2.2 % @Temperature 23.0 °C | 2.0 - 2.2 % @Temperature 73.4 °F | 50% r.h.; ISO 62 | ||
Water Absorption at Saturation | 5.7 - 6.3 % @Time 82800 sec | 5.7 - 6.3 % @Time 23.0 hour | ISO 62 | ||
Linear Mold Shrinkage, Flow | 0.0024 cm/cm | 0.0024 in/in | ISO 294-4 | ||
Linear Mold Shrinkage, Transverse | 0.0127 cm/cm | 0.0127 in/in | ISO 294-4 | ||
Spiral Flow | 890 cm | 350 in | Cross Section: 7[mm]x3.5[mm]; AKRO | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 185 MPa | 26800 psi | 5 [mm/min]; ISO 527-1/2 | ||
92.5 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec | 13400 psi @Temperature 320 - 347 °F, Time 5000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |||
92.5 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec | 13400 psi @Temperature 266 - 302 °F, Time 20000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |||
Elongation at Break | 3.5 % | 3.5 % | 5 [mm/min]; ISO 527-1/2 | ||
Tensile Modulus | 8.50 GPa | 1230 ksi | 1[mm/min]; ISO 527-1/2 | ||
Flexural Strength | 260 MPa | 37700 psi | 2 [mm/min]; ISO 178 | ||
Flexural Modulus | 7.60 GPa | 1100 ksi | 2 [mm/min]; ISO 178 | ||
Charpy Impact Unnotched | 6.40 J/cm² @Temperature -30.0 °C | 30.5 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | |||
1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
Thermal Properties | Metric | English | Comments | ||
Melting Point | 262 °C | 504 °F | ISO 11357-1/3 | ||
Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | HDT/B; ISO 75-2 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | HDT/A; ISO 75-2 | ||
Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
Glow Wire Test | 650 °C @Thickness 1.60 mm | 1200 °F @Thickness 0.0630 in | ICE 60695-12 | ||
Processing Properties | Metric | English | Comments | ||
Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
Nozzle Temperature | 280 - 295 °C | 536 - 563 °F | |||
Zone 1 | 260 - 300 °C | 500 - 572 °F | |||
Zone 2 | 260 - 300 °C | 500 - 572 °F | |||
Zone 3 | 260 - 300 °C | 500 - 572 °F | |||
Zone 4 | 260 - 300 °C | 500 - 572 °F | |||
Melt Temperature | 280 - 320 °C | 536 - 608 °F | |||
Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
Drying Temperature | 80.0 °C | 176 °F | |||
Dry Time | 4 - 12.0 hour | 4 - 12.0 hour | |||
Injection Pressure | 100 MPa | 14500 psi | |||
Hold Pressure | 75.0 MPa | 10900 psi | |||
Back Pressure | 0.400 - 1.00 MPa | 58.0 - 145 psi | |||
Descriptive Properties | |||||
Rate acc. FMVSS 302 (<100/min) | Passed | ||||
Rate acc. FMVSS 302,(<100/min) | FMVSS 302, >1 [mm] Thickness | ||||
Resistance to Oleic acid | Pass | 100% Conc. at 23°C | |||
Resistance to Acetaldehyde | Fail | 40% Conc. at 23°C | |||
Resistance to Acetic Acid | Pass | 20% Conc. at 23°C | |||
Resistance to Acetone | Pass | 100% Conc. at 23°C | |||
Resistance to Acetonitrile | Pass | 100% Conc. at 23°C | |||
Resistance to Acrylonitrile | Pass | 100% Conc. at 23°C | |||
Resistance to Allyl alcohol | Fail | 96% Conc. at 23°C | |||
Resistance to Amyl alcohol | Pass | 100% Conc. at 23°C | |||
Resistance to Aqueous Ammonia | Pass | 10% Conc. at 23°C | |||
Resistance to Benzene | Fail | 100% Conc. at 40°C | |||
Pass | 100% Conc. at 23°C | ||||
Pass | 100% Conc. at 23°C | ||||
Resistance to Biodiesel | Pass | 100% Conc. at 23°C | |||
Resistance to Boric acid | Fail | 100% Conc. at 23°C | |||
Pass | 10% Conc. at 23°C | ||||
Resistance to Brake fluid (DOT 4) | Fail | 100% Conc. at 130°C | |||
Pass | 100% Conc. at 23°C | ||||
Resistance to Calcium chloride, alcoholic | Fail | 10% Conc. at 23°C | |||
Resistance to Calcium chloride, aqueous | Pass | 10% Conc. at 23°C | |||
Resistance to Carbonic acid | Pass | 100% Conc. at 60°C | |||
Resistance to Caustic potash solution, aqueous | Pass | 50% Conc. at 23°C | |||
Resistance to Chloracetic acid | Fail | 50% Conc. at 23°C | |||
Resistance to Chlorine | Fail | 100% Conc. at 23°C | |||
Resistance to Chlorine water | Fail | 100% Conc. at 23°C | |||
Resistance to Chromic acid | Fail | 10% Conc. at 23°C | |||
Resistance to Cyclohexane | Pass | 100% Conc. at 23°C | |||
Resistance to Cyclohexanol | Pass | 100% Conc. at 23°C | |||
Resistance to Dichloro-Acetic acid | Fail | 50% Conc. at 23°C | |||
Resistance to Diesel fuel (DIN 51601) | Pass | 100% Conc. at 23°C | |||
Resistance to Ethanol | Pass | 96% Conc. at 23°C | |||
Resistance to Ethylene glycol/water | Fail | 50% Conc. at 120°C | |||
Resistance to Formaldehyde, aqueous | Pass | 10% Conc. at 23°C | |||
Resistance to Formic acid | Fail | 2% Conc. at 23°C | |||
Resistance to Glycerin | Pass | 100% Conc. at 23°C | |||
Resistance to Hydraulic oil H and HL (DIN 51524) | Pass | 100% Conc. at 100°C | |||
Resistance to Hydrogen chloride, gas | Fail | 100% Conc. at 23°C | |||
Resistance to Iso-octanol | Pass | 100% Conc. at 23°C | |||
Resistance to Isopropanol | Pass | 100% Conc. at 23°C | |||
Resistance to Methanol | Pass | 100% Conc. at 23°C | |||
Resistance to Methylene chloride | Fail | 100% Conc. at 23°C | |||
Resistance to Motor oil (SAE 10W-40) | Pass | 100% Conc. at 130°C | |||
Pass | 100% Conc. at 23°C | ||||
Resistance to Natural Gas | Pass | 100% Conc. at 23°C | |||
Resistance to Nitric acid | Fail | 40% Conc. at 23°C | |||
Resistance to Ozone | Fail | 100% Conc. at 23°C | |||
Resistance to Phenol | Fail | 100% Conc. at 23°C | |||
Resistance to Phosphoric acid | Fail | 30% Conc. at 23°C | |||
Resistance to Potassium chloride, aqueous | Pass | 10% Conc. at 23°C | |||
Resistance to Potassium permanganate, aqueous | Fail | 10% Conc. at 23°C | |||
Resistance to Sodium chloride, aqueous | Pass | 10% Conc. at 23°C | |||
Resistance to Sodium hydroxide solution, aqueous | Pass | 1% Conc. at 23°C | |||
Resistance to Sodium hypochlorite, aqueous | Fail | 10% Conc. at 23°C | |||
Resistance to Transmission oil (ATF m 1375.4) | Pass | 100% Conc. at 150°C | |||
Resistance to Urea, aqueous | Pass | 20% Conc. at 23°C | |||
Resistant to Carbon disulphide | Pass | 100% Conc. at 23°C | |||
Resistant to Carbon tetrachloride | Pass | 100% Conc. at 23°C | |||
Resistant to Citric acid | Pass | 10% Conc. at 23°C | |||
Resistant to Ethyl acetate | Pass | 100% Conc. at 23°C | |||
Resistant to Hydrochloric acid | Fail | 36% Conc. at 23°C | |||
Resistant to Hydrogen peroxide | Fail | 23°C | |||
Resistant to Seawater | Pass | 100% Conc. at 23°C | |||
Resistant to Silicone fluid | Pass | 23°C | |||
Resistant to Sulphuric acid | Fail | 96% Conc. at 23°C | |||
Resistant to Super-grade petrol (DIN 51600) | Pass | 100% Conc. at 23°C | |||
Resistant to Toluol | Pass | 100% Conc. at 23°C | |||
Resistant to Water | Pass | 100% Conc. up to 50°C | |||
Resistant to Xylol | Pass | 100% Conc. at 23°C | |||
Resistant to Zinc chloride, aqueous | Fail | 50% Conc. at 23°C |