- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 1.3
- 弯曲模量 [MPa]: 15.2
- 热变形温度 [℃]: 260.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.57 g/cc @Temperature 23.0 °C | 0.0567 lb/in³ @Temperature 73.4 °F | ISO 1183 | ||
Filler Content | 50 % | 50 % | ISO 1172 | ||
Water Absorption | 1.3 - 1.5 % @Temperature 23.0 °C | 1.3 - 1.5 % @Temperature 73.4 °F | 50% r.h.; ISO 62 | ||
Water Absorption at Saturation | 3.7 - 4.3 % @Time 82800 sec | 3.7 - 4.3 % @Time 23.0 hour | ISO 62 | ||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ISO 294-4 | ||
Linear Mold Shrinkage, Transverse | 0.0116 cm/cm | 0.0116 in/in | ISO 294-4 | ||
Spiral Flow | 600 cm | 236 in | Cross Section: 7[mm]x3.5[mm]; AKRO | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 250 MPa | 36300 psi | 5 [mm/min]; ISO 527-1/2 | ||
125 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec | 18100 psi @Temperature 320 - 347 °F, Time 5000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |||
125 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec | 18100 psi @Temperature 266 - 302 °F, Time 20000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |||
Elongation at Break | 2.5 % | 2.5 % | 5 [mm/min]; ISO 527-1/2 | ||
Tensile Modulus | 16.7 GPa | 2420 ksi | 1[mm/min]; ISO 527-1/2 | ||
9.00 GPa @Temperature 120 °C | 1310 ksi @Temperature 248 °F | ||||
11.0 GPa @Temperature 80.0 °C | 1600 ksi @Temperature 176 °F | ||||
18.0 GPa @Temperature 23.0 °C | 2610 ksi @Temperature 73.4 °F | ||||
Flexural Strength | 380 MPa | 55100 psi | 2 [mm/min]; ISO 178 | ||
Flexural Modulus | 15.2 GPa | 2200 ksi | 2 [mm/min]; ISO 178 | ||
Shear Modulus | 0.100 GPa @Temperature 350 °C | 14.5 ksi @Temperature 662 °F | |||
0.600 GPa @Temperature 300 °C | 87.0 ksi @Temperature 572 °F | ||||
0.700 GPa @Temperature 250 °C | 102 ksi @Temperature 482 °F | ||||
1.00 GPa @Temperature 200 °C | 145 ksi @Temperature 392 °F | ||||
1.50 GPa @Temperature 150 °C | 218 ksi @Temperature 302 °F | ||||
2.50 GPa @Temperature 100 °C | 363 ksi @Temperature 212 °F | ||||
3.00 GPa @Temperature 0.000 °C | 435 ksi @Temperature 32.0 °F | ||||
Charpy Impact Unnotched | 10.5 J/cm² @Temperature -30.0 °C | 50.0 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
10.5 J/cm² @Temperature 23.0 °C | 50.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
Charpy Impact, Notched | 1.60 J/cm² @Temperature -30.0 °C | 7.61 ft-lb/in² @Temperature -22.0 °F | |||
1.90 J/cm² @Temperature 23.0 °C | 9.04 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 9.44 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/2 | ||
CTE, linear, Transverse to Flow | 88.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 48.9 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/2 | ||
Melting Point | 262 °C | 504 °F | ISO 11357-1/3 | ||
Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | HDT/B; ISO 75-2 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | HDT/A; ISO 75-2 | ||
Deflection Temperature at 8.0 MPa | 235 °C | 455 °F | HDT/C; ISO 75-2 | ||
Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
Glow Wire Test | 650 °C @Thickness 1.60 mm | 1200 °F @Thickness 0.0630 in | ICE 60695-12 | ||
Processing Properties | Metric | English | Comments | ||
Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
Nozzle Temperature | 280 - 295 °C | 536 - 563 °F | |||
Zone 1 | 260 - 300 °C | 500 - 572 °F | |||
Zone 2 | 260 - 300 °C | 500 - 572 °F | |||
Zone 3 | 260 - 300 °C | 500 - 572 °F | |||
Zone 4 | 260 - 300 °C | 500 - 572 °F | |||
Melt Temperature | 280 - 320 °C | 536 - 608 °F | |||
Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
Drying Temperature | 80.0 °C | 176 °F | |||
Dry Time | 4 - 12.0 hour | 4 - 12.0 hour | |||
Injection Pressure | 100 MPa | 14500 psi | |||
Hold Pressure | 75.0 MPa | 10900 psi | |||
Back Pressure | 0.400 - 1.00 MPa | 58.0 - 145 psi | |||
Descriptive Properties | |||||
Rate acc. FMVSS 302 (<100/min) | Passed | ||||
Rate acc. FMVSS 302,(<100/min) | FMVSS 302, >1 [mm] Thickness | ||||
Resistance to Oleic acid | Pass | 100% Conc. at 23°C | |||
Resistance to Acetaldehyde | Fail | 40% Conc. at 23°C | |||
Resistance to Acetic Acid | Pass | 20% Conc. at 23°C | |||
Resistance to Acetone | Pass | 100% Conc. at 23°C | |||
Resistance to Acetonitrile | Pass | 100% Conc. at 23°C | |||
Resistance to Acrylonitrile | Pass | 100% Conc. at 23°C | |||
Resistance to Allyl alcohol | Fail | 96% Conc. at 23°C | |||
Resistance to Amyl alcohol | Pass | 100% Conc. at 23°C | |||
Resistance to Aqueous Ammonia | Pass | 10% Conc. at 23°C | |||
Resistance to Benzene | Fail | 100% Conc. at 40°C | |||
Pass | 100% Conc. at 23°C | ||||
Pass | 100% Conc. at 23°C | ||||
Resistance to Biodiesel | Pass | 100% Conc. at 23°C | |||
Resistance to Boric acid | Fail | 100% Conc. at 23°C | |||
Pass | 10% Conc. at 23°C | ||||
Resistance to Brake fluid (DOT 4) | Fail | 100% Conc. at 130°C | |||
Pass | 100% Conc. at 23°C | ||||
Resistance to Calcium chloride, alcoholic | Fail | 10% Conc. at 23°C | |||
Resistance to Calcium chloride, aqueous | Pass | 10% Conc. at 23°C | |||
Resistance to Carbonic acid | Pass | 100% Conc. at 60°C | |||
Resistance to Caustic potash solution, aqueous | Pass | 50% Conc. at 23°C | |||
Resistance to Chloracetic acid | Fail | 50% Conc. at 23°C | |||
Resistance to Chlorine | Fail | 100% Conc. at 23°C | |||
Resistance to Chlorine water | Fail | 100% Conc. at 23°C | |||
Resistance to Chromic acid | Fail | 10% Conc. at 23°C | |||
Resistance to Cyclohexane | Pass | 100% Conc. at 23°C | |||
Resistance to Cyclohexanol | Pass | 100% Conc. at 23°C | |||
Resistance to Dichloro-Acetic acid | Fail | 50% Conc. at 23°C | |||
Resistance to Diesel fuel (DIN 51601) | Pass | 100% Conc. at 23°C | |||
Resistance to Ethanol | Pass | 96% Conc. at 23°C | |||
Resistance to Ethylene glycol/water | Fail | 50% Conc. at 120°C | |||
Resistance to Formaldehyde, aqueous | Pass | 10% Conc. at 23°C | |||
Resistance to Formic acid | Fail | 2% Conc. at 23°C | |||
Resistance to Glycerin | Pass | 100% Conc. at 23°C | |||
Resistance to Hydraulic oil H and HL (DIN 51524) | Pass | 100% Conc. at 100°C | |||
Resistance to Hydrogen chloride, gas | Fail | 100% Conc. at 23°C | |||
Resistance to Iso-octanol | Pass | 100% Conc. at 23°C | |||
Resistance to Isopropanol | Pass | 100% Conc. at 23°C | |||
Resistance to Methanol | Pass | 100% Conc. at 23°C | |||
Resistance to Methylene chloride | Fail | 100% Conc. at 23°C | |||
Resistance to Motor oil (SAE 10W-40) | Pass | 100% Conc. at 130°C | |||
Pass | 100% Conc. at 23°C | ||||
Resistance to Natural Gas | Pass | 100% Conc. at 23°C | |||
Resistance to Nitric acid | Fail | 40% Conc. at 23°C | |||
Resistance to Ozone | Fail | 100% Conc. at 23°C | |||
Resistance to Phenol | Fail | 100% Conc. at 23°C | |||
Resistance to Phosphoric acid | Fail | 30% Conc. at 23°C | |||
Resistance to Potassium chloride, aqueous | Pass | 10% Conc. at 23°C | |||
Resistance to Potassium permanganate, aqueous | Fail | 10% Conc. at 23°C | |||
Resistance to Sodium chloride, aqueous | Pass | 10% Conc. at 23°C | |||
Resistance to Sodium hydroxide solution, aqueous | Pass | 1% Conc. at 23°C | |||
Resistance to Sodium hypochlorite, aqueous | Fail | 10% Conc. at 23°C | |||
Resistance to Transmission oil (ATF m 1375.4) | Pass | 100% Conc. at 150°C | |||
Resistance to Urea, aqueous | Pass | 20% Conc. at 23°C | |||
Resistant to Carbon disulphide | Pass | 100% Conc. at 23°C | |||
Resistant to Carbon tetrachloride | Pass | 100% Conc. at 23°C | |||
Resistant to Citric acid | Pass | 10% Conc. at 23°C | |||
Resistant to Ethyl acetate | Pass | 100% Conc. at 23°C | |||
Resistant to Hydrochloric acid | Fail | 36% Conc. at 23°C | |||
Resistant to Hydrogen peroxide | Fail | 23°C | |||
Resistant to Seawater | Pass | 100% Conc. at 23°C | |||
Resistant to Silicone fluid | Pass | 23°C | |||
Resistant to Sulphuric acid | Fail | 96% Conc. at 23°C | |||
Resistant to Super-grade petrol (DIN 51600) | Pass | 100% Conc. at 23°C | |||
Resistant to Toluol | Pass | 100% Conc. at 23°C | |||
Resistant to Water | Pass | 100% Conc. up to 50°C | |||
Resistant to Xylol | Pass | 100% Conc. at 23°C | |||
Resistant to Zinc chloride, aqueous | Fail | 50% Conc. at 23°C |