- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 8.5
- 拉伸强度 [MPa]: 85.0
- 断裂伸长率 [%]: 130
- 弯曲模量 [MPa]: 3.14
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO data |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 8.5 % | 8.5 % | in water; 23°C; ISO data |
| Viscosity Measurement | 55 | 55 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ASTM value at 50 mm/min. |
| 86.0 MPa | 12500 psi | ISO value at 50 mm/min. | |
| Elongation at Break | 15 % | 15 % | Nominal strain at break, ISO, 50 mm/min |
| 15 % | 15 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 5.0 % | 5.0 % | ISO Value at 50 mm/min. |
| 5.0 % | 5.0 % | ASTM Value at 50 mm/min. | |
| Flexural Yield Strength | 130 MPa | 18900 psi | ASTM Data |
| Flexural Modulus | 3.14 GPa | 455 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ASTM Data |
| 80.0 °C | 176 °F | ISO data | |
| Flammability, UL94 | V-2 @Thickness 0.700 mm | V-2 @Thickness 0.0276 in | |
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |