- 熔体流动速率 [g/10min]: 18.0
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 2.8
- 拉伸强度 [MPa]: 40.0
- 热变形温度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Water Absorption | 2.8 % | 2.8 % | |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | Humidity Absorption |
| Melt Flow | 18 g/10 min @Load 5.00 kg, Temperature 275 °C | 18 g/10 min @Load 11.0 lb, Temperature 527 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.2 % | 4.2 % | 50 mm/min |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 1.9 @Frequency 100 Hz | 1.9 @Frequency 100 Hz | |
| 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 130 µm/m-°C @Temperature 20.0 °C | 72.2 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 142 µm/m-°C @Temperature 20.0 °C | 78.9 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 255 °C | 491 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 148 °C | 298 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||