- 密度 [g/cm3]: 1.51
- 缺口冲击强度: 0.96
- 弯曲强度 [MPa]: 163.0
- 弯曲模量 [MPa]: 9.40
- 硬度: 117.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Ultimate | 163 MPa | 23600 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
| Flexural Modulus | 9.40 GPa | 1360 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D256 |
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours). |
| Limiting Pressure Velocity | 0.700 MPa-m/sec | 20000 psi-ft/min | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 271 - 285 °C | 520 - 545 °F | Approximate middle barrel temperature range |