- 密度 [g/cm3]: 1.64
- 缺口冲击强度: 0.32
- 弯曲强度 [MPa]: 95.0
- 弯曲模量 [MPa]: 10.4
- 硬度: 118.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 95.0 MPa | 13800 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 139 MPa | 20200 psi | ASTM D790 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.08 J/cm | 3.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 236 °C | 457 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 271 - 285 °C | 520 - 545 °F | Approximate middle barrel temperature range |