- 缺口冲击强度: 0.641
- 弯曲模量 [MPa]: 9.9133
- 热变形温度 [℃]: 253.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 3.175 mm | 0.0040 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 169 MPa | 24500 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 225 MPa | 32700 psi | ASTM D790 |
| Flexural Modulus | 9.9133 GPa | 1437.8 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 239 °C | 462 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |