- 缺口冲击强度: 0.427
- 弯曲模量 [MPa]: 4.82
- 热变形温度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm @Thickness 3.175 mm | 0.0090 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 99.3 MPa | 14400 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 161 MPa | 23300 psi | ASTM D790 |
| Flexural Modulus | 4.82 GPa | 699 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.06 J/cm | 7.60 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |