- 密度 [g/cm3]: 1.18
- 缺口冲击强度: 1.23
- 弯曲强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 3.66
- 热变形温度 [℃]: 243.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 6.0 % | 6.0 % | 5mm/min; ISO 527 | ||
| 10 % | 10 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 5.10 GPa | 740 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 152 MPa | 22000 psi | ASTM Test | ||
| Flexural Modulus | 3.66 GPa | 531 ksi | ASTM Test | ||
| 4.70 GPa | 682 ksi | ISO Data | |||
| Izod Impact, Notched | 1.23 J/cm @Thickness 3.17 mm | 2.30 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179 | ||
| 5.50 J/cm² @Temperature -30.0 °C | 26.2 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 | ||
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM Test | ||
| 256 °C | 493 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM Test | ||
| 240 °C | 464 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||