- 熔体流动速率 [g/10min]: 40.0
- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 8.5
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 2.76
- 热变形温度 [℃]: 199.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.5 % | 8.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 3.5 cP | 3.5 cP | ISO Test; 96 % SAV | ||
| Viscosity Test | 205 cm³/g | 205 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM Data; MD | ||
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 275 °C | 40 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50mm/min; ISO 527 | ||
| 80.0 MPa | 11600 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | 25 % | 25 % | 50mm/min, Nominal strain; ISO 527 | ||
| 50 % | 50 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 4.2 % | 4.2 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 3.20 GPa | 464 ksi | 1mm/min; ISO 527 | ||
| 3.20 GPa | 464 ksi | ASTM Test | |||
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.530 J/cm @Temperature -40.0 °C | 0.993 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.640 J/cm @Thickness 3.17 mm | 1.20 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | NB | NB | ISO 179 | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0050 @Frequency 100 Hz | 0.0050 @Frequency 100 Hz | IEC 60250 | ||
| 0.026 @Frequency 1.00e+6 Hz | 0.026 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 22.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 85.0 µm/m-°C | 47.2 µin/in-°F | ISO 11359 | ||
| Melting Point | 255 °C | 491 °F | 10 K/min | ||
| 260 °C | 500 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM Test | ||
| 220 °C | 428 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 | ||
| 100 °C | 212 °F | ASTM Test | |||
| Vicat Softening Point | 250 °C | 482 °F | (50 °C/h / 50N) - B/50; ISO 306 | ||
| Flammability, UL94 | V-2 @Thickness 1.57 mm | V-2 @Thickness 0.0618 in | |||
| V-2 @Thickness 0.890 mm | V-2 @Thickness 0.0350 in | ||||
| Oxygen Index | 28 % | 28 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1500 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Film Extrusion | ||||
| Processing | Injection Molding | ||||
| Other Extrusion | |||||