- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 8.0
- 缺口冲击强度: 0.48
- 拉伸强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 3.13
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.5 - 3.1 % | 2.5 - 3.1 % | 23°C/50% R.H.; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527 | ||
| Flexural Modulus | 3.13 GPa | 454 ksi | ISO Data | ||
| Izod Impact, Notched | 0.480 J/cm @Temperature -40.0 °C | 0.899 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO Test | ||
| 3.50 kJ/m² @Temperature -40.0 °C | 1.67 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK00464 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||