- 密度 [g/cm3]: 1.5
- 缺口冲击强度: 4.2
- 弯曲强度 [MPa]: 135.0
- 弯曲模量 [MPa]: 6.90
- 热变形温度 [℃]: 255.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 10.8 GPa | 1570 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM Test | ||
| 9.80 GPa | 1420 ksi | ISO Data | |||
| Izod Impact, Notched (ISO) | 4.20 kJ/m² | 2.00 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179 | ||
| 4.00 J/cm² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.380 J/cm² | 1.81 ft-lb/in² | ISO 179 | ||
| 0.350 J/cm² @Temperature -30.0 °C | 1.67 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 241 °C | 466 °F | ASTM Test | ||
| 242 °C | 468 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||