- 熔体流动速率 [g/10min]: 40.0
- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 3.7
- 缺口冲击强度: 20.0
- 拉伸强度 [MPa]: 130.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | ||
| Water Absorption | 3.7 - 4.3 % | 3.7 - 4.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.70 - 1.1 % | 0.70 - 1.1 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 140 | 140 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | restricted | ||
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 275 °C | 40 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 130 MPa | 18900 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | ISO 527-1/-2 | ||
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.60 J/cm² @Temperature 23.0 °C | 7.61 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 5400 MPa @Strain <=0.500 % | 783000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.0 @Frequency 1.00 Hz | 5.0 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Hot Wire Ignition, HWI | 1.0 sec @Thickness >=0.800 mm | 1.0 sec @Thickness >=0.0315 in | ASTM D3874-88 | ||
| High Amp Arc Ignition, HAI | 1.0 arcs @Thickness >=0.800 mm | 1.0 arcs @Thickness >=0.0315 in | UL 746C | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | for 50% loss of tensile strength after 20000hr | ||
| 145 °C | 293 °F | for 50% loss of tensile strength after 5000hr | |||
| 220 °C | 428 °F | ||||
| Decomposition Temperature | >= 310 °C | >= 590 °F | |||
| UL RTI, Electrical | 115 °C @Thickness 1.50 mm | 239 °F @Thickness 0.0591 in | UL 746B | ||
| Oxygen Index | 28 % | 28 % | Limiting; ISO 4589-2 | ||
| Glow Wire Test | 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 295 °C | 563 °F | Feed Zone | ||
| Zone 2 | 295 °C | 563 °F | Compression | ||
| Zone 3 | 295 °C | 563 °F | Metering-zone | ||
| Zone 4 | 295 °C | 563 °F | Nozzle | ||
| Melt Temperature | 290 - 300 °C | 554 - 572 °F | Injection-molding/Extrusion | ||
| 295 °C | 563 °F | Optimal | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| 85.0 °C | 185 °F | Optimal | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 23187 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >350°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||