- 熔体流动速率 [g/10min]: 27.2
- 密度 [g/cm3]: 1.36
- 弯曲模量 [MPa]: 8.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 | ||
| 5.4 % | 5.4 % | Saturation; ISO 62 | |||
| Melt Flow | 27.2 g/10 min @Load 5.00 kg, Temperature 275 °C | 27.2 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 | ||
| Tensile Modulus | 9.50 GPa | 1380 ksi | ISO 527 | ||
| Flexural Strength | 280 MPa | 40600 psi | ISO 178 | ||
| Flexural Modulus | 8.70 GPa | 1260 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C | 33.3 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK 20560 | ||||
| Commercial Status | North America | ||||