- 密度 [g/cm3]: 1.15
- 拉伸强度 [MPa]: 51.0
- 弯曲模量 [MPa]: 2.77
- 热变形温度 [℃]: 192.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 | ||
| Elongation at Yield | 3.8 % | 3.8 % | ISO 527 | ||
| Tensile Modulus | 2.96 GPa | 429 ksi | ISO 527 | ||
| Flexural Strength | 86.0 MPa | 12500 psi | ISO 178 | ||
| Flexural Modulus | 2.77 GPa | 402 ksi | ISO 178 | ||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 305 °C | 536 - 581 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.12 % | <= 0.12 % | |||
| Descriptive Properties | |||||
| Color | BK 30564 | ||||
| Commercial Status | North America | ||||