- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 0.64
- 断裂伸长率 [%]: 193
- 弯曲强度 [MPa]: 138.0
- 弯曲模量 [MPa]: 6.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 282 °C | 540 °F | |