- 密度 [g/cm3]: 1.46
- 缺口冲击强度: 0.854
- 拉伸强度 [MPa]: 165.0
- 断裂伸长率 [%]: 234
- 弯曲模量 [MPa]: 11.0
- 热变形温度 [℃]: 257.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 165 MPa | 24000 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 234 MPa | 34000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Temperature 22.8 °C | 1.60 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 494 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 249 - 282 °C | 480 - 540 °F | |
| Middle Barrel Temperature | 254 - 288 °C | 490 - 550 °F | |
| Front Barrel Temperature | 260 - 293 °C | 500 - 560 °F | |
| Nozzle Temperature | 266 - 299 °C | 510 - 570 °F | |
| Melt Temperature | 260 - 293 °C | 500 - 560 °F | |
| Mold Temperature | 79.4 - 135 °C | 175 - 275 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C | 2 - 4 hour @Temperature 175 °F | to avoid degradation of mechanical properties |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 75 rpm | 75 rpm | |