- 密度 [g/cm3]: 1.09
- 缺口冲击强度: 5.34
- 拉伸强度 [MPa]: 42.1
- 断裂伸长率 [%]: 51.7
- 弯曲模量 [MPa]: 1.52
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 - 0.019 cm/cm | 0.014 - 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 42.1 MPa | 6100 psi | ASTM D638 |
| Elongation at Yield | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 51.7 MPa | 7500 psi | ASTM D790 |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Temperature -40.0 °C | 10.0 ft-lb/in @Temperature -40.0 °F | ASTM D256 |
| 9.08 J/cm @Temperature 22.8 °C | 17.0 ft-lb/in @Temperature 73.0 °F | ASTM D256 | |
| Gardner Impact | 12.2 J @Temperature -40.0 °C | 9.00 ft-lb @Temperature -40.0 °F | ASTM D3673 |
| 38.0 J @Temperature 22.8 °C | 28.0 ft-lb @Temperature 73.0 °F | ASTM D3673 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 266 - 288 °C | 510 - 550 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C | 2 - 4 hour @Temperature 175 °F | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |