Clariant Renol PA133G33 Nylon 66, 33% Glass Fiber, Highly Impact Modified

Clariant Renol PA133G33 Nylon 66, 33% Glass Fiber, Highly Impact Modified 物性表: Clariant Renol PA133G33 Nylon 66, 33% Glass Fiber, Highly Impact Modified物性表及特性介绍,Clariant Renol PA133G33 Nylon 66, 33% Glass Fiber, Highly Impact Modified注塑参数详情,如需Clariant Renol PA133G33 Nylon 66, 33% Glass Fiber, Highly Impact Modified下载, 可到相关下载区下载
  • 缺口冲击强度: 2.03
  • 拉伸强度 [MPa]: 124.0
  • 断裂伸长率 [%]: 179
  • 弯曲模量 [MPa]: 5.52
  • 热变形温度 [℃]: 250.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.32 g/cc1.32 g/ccASTM D792
Linear Mold Shrinkage, Flow 0.0060 cm/cm0.0060 in/inASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 124 MPa18000 psiASTM D638
Elongation at Yield 4.0 %4.0 %ASTM D638
Flexural Yield Strength 179 MPa26000 psiASTM D790
Flexural Modulus 5.52 GPa800 ksiASTM D790
Izod Impact, Notched 2.03 J/cm
@Temperature 22.8 °C
3.80 ft-lb/in
@Temperature 73.0 °F
ASTM D256
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 250 °C482 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 220 °C428 °FASTM D648
 
Processing PropertiesMetricEnglishComments
Melt Temperature 266 - 293 °C510 - 560 °F
Mold Temperature 79.4 - 107 °C175 - 225 °F
Dry Time 2 - 4 hour
@Temperature 79.4 °C
2 - 4 hour
@Temperature 175 °F
to ensure moisture content is less than 0.2%
Injection Pressure 4.96 - 8.27 MPa720 - 1200 psiSecondary
 8.27 - 13.8 MPa1200 - 2000 psiInitial
Back Pressure 0.345 - 1.72 MPa50.0 - 250 psi
Shot Size 30 - 80 %30 - 80 %
Screw Speed 20 - 100 rpm20 - 100 rpm

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45307.html

免责声明: 本文 Clariant Renol PA133G33 Nylon 66, 33% Glass Fiber, Highly Impact Modified 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4