- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 1.0
- 缺口冲击强度: 0.5
- 弯曲强度 [MPa]: 107.0
- 弯曲模量 [MPa]: 4.80
- 硬度: 120.0
- 热变形温度 [℃]: 238.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 107 MPa | 15500 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Compressive Yield Strength | 179 MPa | 26000 psi | ASTM D695 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 263 °C | 505 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |