- 密度 [g/cm3]: 1.42
- 成型收缩率 [%]: 0.002
- 缺口冲击强度: 0.43
- 弯曲模量 [MPa]: 6.90
- 热变形温度 [℃]: 252.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | DAM; ASTM D792 | ||
| Density | 1.42 g/cc | 0.0513 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 36 % | 36 % | DAM | ||
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 1.60 mm | 0.0020 in/in @Thickness 0.0630 in | Flow; DAM | ||
| 0.0040 cm/cm @Thickness 6.40 mm | 0.0040 in/in @Thickness 0.252 in | Flow; DAM | |||
| 0.0040 cm/cm @Thickness 3.20 mm | 0.0040 in/in @Thickness 0.126 in | Flow; DAM | |||
| 0.0080 cm/cm @Thickness 1.60 mm | 0.0080 in/in @Thickness 0.0630 in | Transverse; DAM | |||
| 0.0090 cm/cm @Thickness 3.20 mm | 0.0090 in/in @Thickness 0.126 in | Transverse; DAM | |||
| 0.010 cm/cm @Thickness 6.40 mm | 0.010 in/in @Thickness 0.252 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 75.0 MPa @Temperature 23.0 °C | 10900 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 105 MPa @Temperature 23.0 °C | 15200 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Elongation at Break | 2.2 % @Temperature 23.0 °C | 2.2 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 6.20 GPa @Temperature 23.0 °C | 899 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 159 MPa @Temperature 23.0 °C | 23100 psi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| Flexural Modulus | 6.90 GPa @Temperature 23.0 °C | 1000 ksi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| 8.00 GPa @Temperature 23.0 °C | 1160 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched | 0.430 J/cm @Temperature 23.0 °C | 0.806 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| 0.530 J/cm @Temperature 23.0 °C | 0.993 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
| Izod Impact, Unnotched | 4.80 J/cm @Temperature 23.0 °C | 8.99 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 0.250 J/cm² @Temperature -40.0 °C | 1.19 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 45.0 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 81.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 45.0 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 263 °C | 505 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | DAM; ASTM D648 | ||
| 255 °C | 491 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | DAM; ISO 75-1/-2 | ||
| 235 °C | 455 °F | DAM; ASTM D648 | |||
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Glass/Mineral | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-I(MD+GF)36< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass/Mineral Reinforced Resins | DAM | |||
| Low Warp Resins | DAM | ||||
| Resin Identification | PA66-I(MD+GF)36 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||